保护渣在连铸机中的应用

  • 钟云涛1,李强2,3
作者信息 +

Application of Mold Powder in Continuous Casting Machine

  • 钟云涛1,李强2,3
Author information +
文章历史 +

摘要

结晶器保护渣在连铸浇注过程中起着非常重要的作用,其功能主要是在连铸结晶器内发挥着绝热保温、防止钢液氧化、控制传热、润滑铸坯的作用,是促进连铸技术发展、保证连铸工艺顺行及铸坯质量的关键性材料。鉴于其重要性,仔细地分析和研究了连铸保护渣的各种物理化学性能,并结合钢种和铸坯断面等工艺条件,系统地分析了保护渣性能对浇注的影响和如何正确的选择保护渣。

Abstract

Mold powder is a very significant and critical material and takes a key role during casting. The main functions of the mold powder are to play insulation, prevent re-oxidation, control heat transfer of liquid steel, and lubricate shell. It is a key material to promote the development of continuous casting technology, and ensure the smooth process of continuous casting and quality of casting. In view of its importance, various physical and chemical properties of mold powder, are detailed analyzed combined with steel types and cast section and other conditions, systematic analysis on the impact of performance of mold powder and how to choose the correct mold powder are also discussed.

关键词

连铸 / 保护渣 / 粘度 / 碱度.

Key words

casting / mold powder / viscosity / alkalinity.

图表

引用本文

导出引用
钟云涛, 李强, 武文辉. 保护渣在连铸机中的应用[J]. 连铸, 2013, 32(4): 9-13
ZHONG Yun-Shou, LI Jiang, WU Wen-Hui. Application of Mold Powder in Continuous Casting Machine[J]. Continuous Casting, 2013, 32(4): 9-13

参考文献

参考文献:
[1] Brimacombe J K. 板坯振痕的形成[A ]. 重庆大学连铸保护渣译文集[C ]. 重庆: 重庆大学冶金系, 1986. 1162125.
[2] F.Neumann et a1.Mold Fluxes in High Speed Thin Slab Casting.Steelmaking Conference
Proceedings,1996:249-257.
[3]. 飯田孝道ほか?多成分系熔融フラックスの粘度推算式。材料とプロセス、1995,8:1014.
[4] 川本正辛ほか?高速連鋳用バウダーの特性設計、鉄と鋼,1994,3:219.224.
[5] 中野武人王扎连铸铸片?纵割バウダーの铸型内熔融,フラックスの影响,铁钢,1981,8:1210.1215.
[6] I.R.Lee.Development ofMould Powder for High Speed Continuous asting.Conference On Continuous Casting of Steel in Developing Countries.Conference Proceedings,Beijing,1993.
[7] C.A.Pinheiro.MoldFluxforCCofSteel.Iron and Steelmaker,1996,23(3):85
[8] S.Ogibayashi et a1.Mold Powder Technology for Continuous Casting of Low-Carbon Aluminum-Killed Steel.Nippon S/eel Technical Report,1987.34(7):1一10.
[9] 袁伟霞.连铸板坯表面星状裂纹的形成与控制.钢铁研究,1998,5:24.27.
[10] 郭上型,董元箎,陈二保,等,CaO-SiO2-Fe2O3-MnO2-MgO-P2O5系溶剂对钢液脱磷、回磷的实验研究[J],钢铁,2000,35(3):19-21.

10

Accesses

0

Citation

Detail

段落导航
相关文章

/