针对某型氧脱硫塔贫溶剂泵在正常工况下进行作业时其泵轴发生断裂,进行了原因分析以及提出改进措施。首先对失效泵轴进行宏观分析,根据实际断裂特点确定其断裂形式,然后在轴断面选择一点进行金相分析,其次分析失效泵轴的化学成分,最后运用扫描电镜对轴断面进行微观分析,并且在韧窝区和沿晶区进行了能谱对比,发现各区元素并无明显差异,基于以上分析,得出泵轴断裂失效原因可能与轴的异常磨损和不当的热处理工艺有关,同时提出有针对性的预防措施。
Abstract
Aiming at the fracture of pump shaft of a lean solvent pump in an oxygen desulfurization tower under normal working conditions, the causes were analyzed and the improvement measures were put forward. Firstly, the failure pump shaft was analyzed macroscopically, and the fracture form was determined according to the actual fracture characteristics. Then, the metallographic analysis was carried out at a point of the shaft section. Thirdly, the chemical composition of the failure pump shaft was analyzed. Finally, the fracture section of shaft was analyzed microscopically using scanning electron microscope. The energy spectrum comparison was carried out in the dimple region and the intergranular region. It was found that the elements in various areas had no significant difference. Based on the analyses above, the fracture failure of the pump shaft may be related to the abnormal wear and improper heat treatment process of the shaft, and meanwhile, the corresponding preventive measures were proposed.
关键词
断裂 /
预防措施 /
泵轴 /
失效分析
{{custom_keyword}} /
Key words
crack /
pump shaft /
preventive measure /
failure analysis
{{custom_keyword}} /
{{custom_sec.title}}
{{custom_sec.title}}
{{custom_sec.content}}
参考文献
[1] 李露水,刘课秀,刘昭杰,等. 汽车起重机钢丝绳的断裂原因[J]. 物理测试,2022,40(2):42.
[2] 国家技术监督局. GB/T 1220—2007不锈钢棒[S].北京:中国标准出版社,2007.
[3] 刘海波,王君,沈源,等. 气缸盖螺栓断裂失效分析[J]. 物理测试,2021,39(4):37.
[4] 魏玉伟,彭安校,苏兰林,等. 氧化铝分解槽焊缝应力—碱脆开裂行为[J]. 有色金属工程,2022,12(7):57.
[5] 李亚红,盛春翔,周绪绪,等. 20CrMnTi钢锻件拉伸性能不合格原因分析[J]. 物理测试,2022,40(2):31.
[6] 魏玉伟,毛明志,李卫超,等. 制氢转化炉下猪尾管爆裂失效原因分析[J]. 中国特种设备安全,2017,33(9):76.
[7] 屈小波,王军,包耀宗. 非调质钢YG1401的冲击韧性和断口形貌探讨[J]. 物理测试,2021,39(6):55.
[8] 王立坤,陈海,魏培生,等. 不锈钢换热管的失效分析[J]. 腐蚀与防护,2020,41(10):74.
[9] 张科,朱丽霞,何志,等. X52输气管道腐蚀失效分析[J]. 腐蚀与防护,2020,41(4):73.
[10] 董莎莎,李南,罗志强. 20CrMnMo减速机高速轴断裂原因分析[J]. 物理测试,2021,39(1):40.
[11] 蔡欣男,王金太,袁姗姗,等. 大功率风力发电机齿轮失效分析[J]. 物理测试,2021,39(4):29.
[12] 林双平,司红,钟振前,等. 汽车减震器活塞杆断裂失效分析[J]. 物理测试,2019,37(1):44.
[13] 胡跃均,陈麒琳,李荣锋,等. 下摆臂断裂失效分析[J]. 物理测试,2020,38(4):40.
[14] 陈义. 水泵轴承的失效分析[J]. 物理测试,2018,36(4):38.
[15] 刘龙,李南,罗志强. 某型装甲车用履带断裂分析[J]. 物理测试,2020,38(2):22.
[16] 陆伟成,廖美华,杨雄强,等. 20MnCr5圆棒锯切困难原因分析[J]. 物理测试,2021,39(4):47.
[17] 王立坤,张宏锋,陈海,等. 焦化装置V401顶安全阀弹簧的断裂原因[J]. 机械工程材料,2019,43(12):71.
[18] 王春芳,李继康,王哲. 50CrVA电机轴断裂原因的分析[J]. 物理测试,2020,38(5):9.
[19] 王亮兵,吴王平,徐飞,等. 某单相断路器连杆的断裂原因[J]. 机械工程材料,2018,42(11):79.
[20] 郭海霞,张金民,张欣耀. 连接体的接头断裂原因分析[J]. 物理测试,2021,39(3):43.
{{custom_fnGroup.title_cn}}
脚注
{{custom_fn.content}}