As the transportation equipment of the large marine ship, cracks were found on the adapter strip of one transfer vehicle during use. The material of the adapter strip was 304 stainless steel. In order to find out the causes for the cracking of the adapter strip, the macro analysis, micro analysis, chemical composition, mechanical properties and metallographic analysis of the adapter strip were carried out by scanning electron microscope, direct reading spectrum, energy spectrometer, metallographic microscope, universal material testing machine and Brinell hardness tester. Through the stress corrosion test, the causes for the crackng of the adapter strip were verified. The results showed that the unqualified material of the adapter strip of the transport vehicle was the main reason for the cracking, and the intergranular corrosion and stress corrosion in the marine environment were the inducing factor for the craking of the adapter strip. Through the vibration aging treatment of the frame and the use of 316L stainless steel with better corrosion resistance, the occurrence of similar incidents could be effectively avoided.
Key words
corrosion /
crack /
adapter strip /
stainless steel
{{custom_keyword}} /
{{custom_sec.title}}
{{custom_sec.title}}
{{custom_sec.content}}
References
[1] 成大先. 机械设计手册[M] 北京:化学工业出版社,2016.
[2] 常国栋,武敏. 某焦化厂煤调湿蒸汽回转干燥机管束失效分析[J].物理测试,2022,40(2):54.
[3] 于雷,杨春,刘明,等. 1Cr18Ni9Ti冷轧不锈钢管表面白斑形成原因分析[J].物理测试,2022,40(3):31.
[4] 朱姣,钟振前,于学亮,等. 304不锈钢焊接管开裂原因分析[J].物理测试,2021,39(5):48.
[5] 刘海定,王东哲,王春光,等.海水环境中不锈钢腐蚀疲劳裂纹研究进展[J].全面腐蚀控制,2017,31(4):60.
[6] 于晓飞. 304、316不锈钢晶间腐蚀的实验与理论研究[D].济南:山东大学,2010.
[7] 吴冰冰,曾志卫,邓番林,等. 某化工厂管道输气用不锈钢法兰漏气裂纹分析[J].物理测试,2021,39(4):42.
[8] 刘帅,朱磊.有关不锈钢应力腐蚀开裂的研究[J].价值工程,2018(20):129.
[9] 沈保罗,李旭初.奥氏体不锈钢产生氯脆的影响因素及对策[J].化工腐蚀与防护,1996(2):18.
[10] 宋凤明,温东辉.磨蚀试验装置研制及疏浚管用钢耐磨蚀评价[J].物理测试,2020,38(1):52.
{{custom_fnGroup.title_en}}
Footnotes
{{custom_fn.content}}