Analysis of factors for Si-Ca-Ba alloy+CaF2 dearsenication of molten steel
LI Wen-bo1,2,BAO Yan-ping1,2,WANG Min1,2,LIN Lu1,2
1. State?Key?Laboratory?of?Advanced?Metallurgy,?University?of?Science?and?Technology?Beijing,? Beijing?100083,China 2. School of Metallurgical and Ecological Engigeering, University of Science and Technology Beijing, Beijing 100083, China
Abstract:To make full use of domestic iron ore containing arsenic, the dearsenication agent of Si-Ca-Ba alloy+CaF2 were researched in laboratory. It has been shown that the ratio of Si-Ca-Ba alloy, temperature, the amount of dearsenicatior and initial sulfur content in molten steel can affect the results of dearsenication. The present results indicate that the ratio of Si-Ca-Ba alloy which is in the range of 65%-75% has the most obvious dearsenication effect. Simultaneously, elevating temperature of molten steel, increasing the amount of dearsenication agent and reducing the initial sulfur content can improve the rate of dearsenication..
李文博,包燕平,王 敏,林 路,. 采用Si-Ca-Ba合金+CaF2进行钢液脱砷的因素分析[J]. 钢铁, 2015, 50(9): 17-22.
LI Wen-bo,,BAO Yan-ping,,WANG Min,,LIN Lu,. Analysis of factors for Si-Ca-Ba alloy+CaF2 dearsenication of molten steel. Iron and Steel, 2015, 50(9): 17-22.