Effect of pretreatment sintering desulfurization ash addition on basic sintering characteristics of iron ore
LUO Yun-fei1, QIAN Li-xin1, LONG Hong-ming1,2, ZHANG Yu-dong1, WEI Ru-fei1
1. School of Metallurgical Engineering, Anhui University of Technology, Ma′anshan 243002, Anhui, China 2. Anhui Province Key Laboratory of Metallurgy Engineering and Resources Recycling(Anhui University of Technology, Ma′anshan 243002, Anhui, China)
Abstract:The most commonly used stacking disposal method of the sintering flue gas semi-dry desulfurization ash takes up land and is prone to secondary pollution. A technical idea of using the pre-treatment desulfurization ash to add into the sintering raw materials by replacement the CaO flux so as to make full use of the flux components was proposed,expecting to realize the closed-circuit resource utilization of the desulfurization ash in metallurgical enterprises. The thermal decomposition of desulfurized ash with carbon and the effect of the addition of pre-treatment desulfurization on the basic characteristics of the iron ore were studied. The results show that adding 1% coke powder can effectively improve the decomposition rate of desulfurization ash and reduce the generation of CaSO4. Meanwhile,with the increasing of the addition proportion of pre-treated desulfurized ash,the assimilation temperature and bond phase strength of the iron ore increases first and then decreases, and the liquid phase fluidity increases monotonously. However,when the substitution ratio exceeds 40% the liquid phase fluidity creates the "false appearance" of great fluidity. The phase structure of the binding phase indicates that the suggested substitution ratio is less than 40%,which is beneficial to the formation of calcium ferrite in the quenched sample. Therefore,the best substitution ratio should be less than 40%.
罗云飞, 钱立新, 龙红明, 章裕东, 魏汝飞. 配加预处理脱硫灰对铁矿烧结基础特性的影响[J]. 钢铁, 2019, 54(12): 117-124.
LUO Yun-fei, QIAN Li-xin, LONG Hong-ming, ZHANG Yu-dong, WEI Ru-fei. Effect of pretreatment sintering desulfurization ash addition on basic sintering characteristics of iron ore. Iron and Steel, 2019, 54(12): 117-124.
姚璐,刘清才,方诗惠,等. 半干法烧结烟气脱硫灰的氧化改性[J]. 环境工程学报,2016,10(6):3147. (YAO Lu,LIU Qing-cai,FANG Shi-hui,et al. Oxidation modification of semi-dry desulfurization ash from sintering flue gas[J]. Chinese Journal of Environmental Engineering,2016,10(6):3147.)
[2]
张瑶,任耘,刘佰龙,等. 烧结脱硫石膏的综合利用现状[J]. 硅酸盐通报,2015,34(12): 3563. (ZHANG Yao,REN Yun,LIU Bai-long,et al. Comprehensive utilization status of sintering flue gas desulfurization gypsum[J]. Bulletin of the Chinese Ceramic Society,2015,34(12):3563.)
[3]
龙红明,王毅璠,吕宁宁,等. 烧结烟气钙基脱硫副产物资源化利用研究进展[J]. 工程研究——跨学科视野中的工程,2017,9(1):78. (LONG Hong-ming,WANG Yi-fan,LÜ Ning-ning,et al. Research development of resource utilization of sintering flue gas calcium based desulfurization byproduct[J]. Journal of Engineering Studies,2017,9(1): 78.)
[4]
WANG C,TAN K,XU X,et al. Effect of activators, admixtures and temperature on the early hydration performance of desulfurization ash[J]. Construction and Building Materials,2014,70:322.
[4]
WANG C,TAN K,XU X,et al. Effect of activators, admixtures and temperature on the early hydration performance of desulfurization ash[J]. Construction and Building Materials,2014,70:322.
[5]
Linek V,Vacek V. Chemical engineering use of catalyzed sulfite oxidation kinetics for the determination of mass transfer characteristics of gas-liquid contactors[J]. Chemical Engineering Science,1981,36(11):1747.
[5]
Linek V,Vacek V. Chemical engineering use of catalyzed sulfite oxidation kinetics for the determination of mass transfer characteristics of gas-liquid contactors[J]. Chemical Engineering Science,1981,36(11):1747.
[6]
Amedeo Lancia,Dino Musmarra,Francesco Pepe. Uncatalyzed heterogeneous oxidation of calcium bisulfite[J]. Chemical Engineering Science,1996,51(16):3889.
[7]
吴晓琴,吴忠标,汪大翚. 均相/非均相体系中亚硫酸钙非催化氧化过程[J]. 环境科学学报,2004,24(3):534. (WU Xiao-qin,WU Zhong-biao,WANG Da-hui. Uncatalyzed oxidation process for calcium sulfite in homogeneous hetero-geneous systems[J]. Acta Scientiae Circumstantiae,2004,24(3):534.)
[8]
杨剑,文娟,董凌燕,等. 烟气脱硫过程锰催化氧化亚硫酸钙的研究[J]. 环境工程学报,2007,1(9):109. (YANG Jian,WEN Juan,DONG Ling-yan,et al. Study on catalytic oxidation of calcium sulfite in flue gas desulfurization process by using manganese sulfate[J]. Chinese Journal of Environmental Engineering,2007,1(9):109.)
[6]
Amedeo Lancia,Dino Musmarra,Francesco Pepe. Uncatalyzed heterogeneous oxidation of calcium bisulfite[J]. Chemical Engineering Science,1996,51(16):3889.
[7]
吴晓琴,吴忠标,汪大翚. 均相/非均相体系中亚硫酸钙非催化氧化过程[J]. 环境科学学报,2004,24(3):534. (WU Xiao-qin,WU Zhong-biao,WANG Da-hui. Uncatalyzed oxidation process for calcium sulfite in homogeneous hetero-geneous systems[J]. Acta Scientiae Circumstantiae,2004,24(3):534.)
[8]
杨剑,文娟,董凌燕,等. 烟气脱硫过程锰催化氧化亚硫酸钙的研究[J]. 环境工程学报,2007,1(9):109. (YANG Jian,WEN Juan,DONG Ling-yan,et al. Study on catalytic oxidation of calcium sulfite in flue gas desulfurization process by using manganese sulfate[J]. Chinese Journal of Environmental Engineering,2007,1(9):109.)
[9]
Ermakov A N,Purmal A P. Catalysis of HSO-3/SO2-sub>3 oxidation by manganese ions[J]. Kinetics and Catalysis,2002,43(2):249.
[9]
Ermakov A N,Purmal A P. Catalysis of HSO-3/SO2-sub>3 oxidation by manganese ions[J]. Kinetics and Catalysis,2002,43(2):249.
[10]
Li Y,Sadakata M. Study of gypsum formation for appropriate dry desulfurization process of flue gas[J]. Fuel,1999,78(9):1089.
[11]
安徽工业大学. 一种利用烧结烟气脱硫副产物制备硫酸钙晶须的方法:中国,201611068287.7[P]. 2017-05-31. (Anhui University of Technology. A method for preparing calcium sulfate whisker by using sintering flue gas desulfurization by-product:China, 201611068287.7[P]. 2017-05-31.)
[10]
Li Y,Sadakata M. Study of gypsum formation for appropriate dry desulfurization process of flue gas[J]. Fuel,1999,78(9):1089.
[11]
安徽工业大学. 一种利用烧结烟气脱硫副产物制备硫酸钙晶须的方法:中国,201611068287.7[P]. 2017-05-31. (Anhui University of Technology. A method for preparing calcium sulfate whisker by using sintering flue gas desulfurization by-product:China, 201611068287.7[P]. 2017-05-31.)
[12]
MIAO M,FENG X,WANG G L,et al. Direct transformation of FGD gypsum to calcium sulfate hemihydrate whiskers:Preparation,simulations,and process analysis[J]. Particuology,2015,19:53.
[12]
MIAO M,FENG X,WANG G L,et al. Direct transformation of FGD gypsum to calcium sulfate hemihydrate whiskers:Preparation,simulations,and process analysis[J]. Particuology,2015,19:53.
[13]
YANG L S,WANG X,ZHU X F,et al. Preparation of calcium sulfate whisker by hydrothermal method from flue gas desulfurization (FGD) gypsum[J]. Applied Mechanics and Materials,2012,270:823.
[14]
史培阳,邓志银,袁义义,等. 利用脱硫石膏水热合成硫酸钙晶须[J]. 东北大学学报:自然科学版,2010,31(1):76.(SHI Pei-yang,DENG Zhi-yin,YUAN Yi-yi,et al. Preparation of calcium sulfate whiskers from desulphurized gypsum by hydrothermal synthesis[J]. Journal of Northeastern University:Natural Science,2010,31(1):76.)
[15]
张玉才,刘佩秋,王宁,等. 脱硫灰返回烧结利用的生产尝试[J]. 烧结球团,2014,39(5):51.(ZHANG Yu-cai,LIU Pei-qiu,WANG Ning,et al. Production trial of utilization of the desulfurization ash returned to sintering[J]. Sintering and Pelletizing,2014,39(5):51.)
[16]
谢皓,王劲松,邹忠平,等. 高炉炉渣脱硫能力分析[J]. 中国冶金,2014,24(12):47.(XIE Hao,WANG Jin-song,ZOU Zhong-ping,et al. Analysis of the desulphurization capacity of blast furnace slag[J]. China Metallurgy,2014,24(12):47.)
[17]
袁骧,张建良,毛瑞,等. 镁铝比对高炉渣脱硫能力的影响[J]. 东北大学学报:自然科学版,2015,36(11):1609.(YUAN Xiang,ZHANG Jian-liang,MAO Rui,et al. Effect of w(MgO)/w(Al2O3) ratio on desulfurization capacity of BF slag[J]. Journal of Northeastern University:Natural Science,2015,36(11):1609.)
[18]
张寿荣,张卫东. 中国钢铁企业固体废弃物资源化处理模式和发展方向[J]. 钢铁,2017,52(4):1.(ZHANG Shou-rong,ZHANG Wei-dong. Solid waste resources treatment mode and development tendency of iron and steel enterprises in China[J]. Iron and Steel,2017,52(4):1.)
[19]
龙红明,魏汝飞,李宁,等. 高炉炼铁协同处理城市可燃固废[J]. 钢铁,2018,53(3):1. (LONG Hong-ming,WEI Ru-fei,LI Ning,et al. Disposal of city combustible solid waste by blast furnace[J]. Iron and Steel,2018,53(3):1.)
[13]
YANG L S,WANG X,ZHU X F,et al. Preparation of calcium sulfate whisker by hydrothermal method from flue gas desulfurization (FGD) gypsum[J]. Applied Mechanics and Materials,2012,270:823.
[20]
常进,张新建,刘清才,等. 添加城市污泥对烧结过程及烧结矿质量的影响[J]. 钢铁研究学报,2017,29(9):711.(CHANG jin,ZHANG Xin-jian,LIU Qing-cai,et al. Effect of sintering raw materials with municipal sludge on sintering process and sinter quality[J]. Journal of Iron and Steel Research, 2017,29(9):711.)
[21]
吴胜利,苏博,齐渊洪,等. 铁矿粉液相流动性的主要液相生成特征因素解析[J]. 工程科学学报,2018,40(3):321.(WU Sheng-li,SU Bo,QI Yuan-hong,et al. Major melt formation characteristic factor analysis of iron ore liquid phase fluidity during the sintering process[J]. Chinese Journal of Engineering,2018,40(3):321.)
[14]
史培阳,邓志银,袁义义,等. 利用脱硫石膏水热合成硫酸钙晶须[J]. 东北大学学报:自然科学版,2010,31(1):76.(SHI Pei-yang,DENG Zhi-yin,YUAN Yi-yi,et al. Preparation of calcium sulfate whiskers from desulphurized gypsum by hydrothermal synthesis[J]. Journal of Northeastern University:Natural Science,2010,31(1):76.)
[22]
范晓慧. 铁矿烧结优化配矿原理与技术[M]. 北京:冶金工业出版社,2013.(FAN Xiao-hui. Principle and Technology of Iron Ore Matching for Sintering[M]. Beijing: Metallurgical Industry Press,2013.)
[15]
张玉才,刘佩秋,王宁,等. 脱硫灰返回烧结利用的生产尝试[J]. 烧结球团,2014,39(5):51.(ZHANG Yu-cai,LIU Pei-qiu,WANG Ning,et al. Production trial of utilization of the desulfurization ash returned to sintering[J]. Sintering and Pelletizing,2014,39(5):51.)
[23]
安徽工业大学. 一种基于电信号变化判断铁矿粉同化温度的方法:中国,201710676858.3[P].2018-05-08.(Anhui University of Technology.A method for judging iron ore powder assimilation temperature based on electric signal change:China, 201710676858.3[P].2018-05-08.)
[16]
谢皓,王劲松,邹忠平,等. 高炉炉渣脱硫能力分析[J]. 中国冶金,2014,24(12):47.(XIE Hao,WANG Jin-song,ZOU Zhong-ping,et al. Analysis of the desulphurization capacity of blast furnace slag[J]. China Metallurgy,2014,24(12):47.)
[24]
龙红明,钱立新,春铁军,等. 基于n(Fe2O3)/n(CaO)的铁矿粉烧结液相流动性测定方法[J]. 中南大学学报:自然科学版,2018,49(7):39.(LONG Hong-ming,QIAN Li-xin,CHUN Tie-jun,et al. Determination method of iron ore liquid phase fluidity index during sintering based on n(Fe2O3)/n(CaO)[J]. Journal of Central South University:Science and Technology,2018,49(7):39.)
[17]
袁骧,张建良,毛瑞,等. 镁铝比对高炉渣脱硫能力的影响[J]. 东北大学学报:自然科学版,2015,36(11):1609.(YUAN Xiang,ZHANG Jian-liang,MAO Rui,et al. Effect of w(MgO)/w(Al2O3) ratio on desulfurization capacity of BF slag[J]. Journal of Northeastern University:Natural Science,2015,36(11):1609.)
[18]
张寿荣,张卫东. 中国钢铁企业固体废弃物资源化处理模式和发展方向[J]. 钢铁,2017,52(4):1.(ZHANG Shou-rong,ZHANG Wei-dong. Solid waste resources treatment mode and development tendency of iron and steel enterprises in China[J]. Iron and Steel,2017,52(4):1.)
[25]
吴胜利,刘宇,杜建新,等. 铁矿石的烧结基础特性之新概念[J]. 北京科技大学学报,2002,24(3):254.(WU Sheng-li,LIU Yu,DU Jian-xin,et al. New concept of iron ores sintering basic characteristics[J]. Journal of University of Science and Technology Beijing,2002,24(3):254.)
[19]
龙红明,魏汝飞,李宁,等. 高炉炼铁协同处理城市可燃固废[J]. 钢铁,2018,53(3):1. (LONG Hong-ming,WEI Ru-fei,LI Ning,et al. Disposal of city combustible solid waste by blast furnace[J]. Iron and Steel,2018,53(3):1.)
[26]
付忠旺,莫朝兴,陈小敏,等. 铁矿粉烧结液相流动性特征数的影响因素[J]. 钢铁,2018,53(12):18.(FU Zhong-wang,MO Chao-xing,CHEN Xiao-min,et al. Influence factors of fluidity characteristic number of iron ore powder[J]. Iron and Steel,2018,53(12):18.)
[20]
常进,张新建,刘清才,等. 添加城市污泥对烧结过程及烧结矿质量的影响[J]. 钢铁研究学报,2017,29(9):711.(CHANG jin,ZHANG Xin-jian,LIU Qing-cai,et al. Effect of sintering raw materials with municipal sludge on sintering process and sinter quality[J]. Journal of Iron and Steel Research, 2017,29(9):711.)
[21]
吴胜利,苏博,齐渊洪,等. 铁矿粉液相流动性的主要液相生成特征因素解析[J]. 工程科学学报,2018,40(3):321.(WU Sheng-li,SU Bo,QI Yuan-hong,et al. Major melt formation characteristic factor analysis of iron ore liquid phase fluidity during the sintering process[J]. Chinese Journal of Engineering,2018,40(3):321.)
[22]
范晓慧. 铁矿烧结优化配矿原理与技术[M]. 北京:冶金工业出版社,2013.(FAN Xiao-hui. Principle and Technology of Iron Ore Matching for Sintering[M]. Beijing: Metallurgical Industry Press,2013.)
[23]
安徽工业大学. 一种基于电信号变化判断铁矿粉同化温度的方法:中国,201710676858.3[P].2018-05-08.(Anhui University of Technology.A method for judging iron ore powder assimilation temperature based on electric signal change:China, 201710676858.3[P].2018-05-08.)
[24]
龙红明,钱立新,春铁军,等. 基于n(Fe2O3)/n(CaO)的铁矿粉烧结液相流动性测定方法[J]. 中南大学学报:自然科学版,2018,49(7):39.(LONG Hong-ming,QIAN Li-xin,CHUN Tie-jun,et al. Determination method of iron ore liquid phase fluidity index during sintering based on n(Fe2O3)/n(CaO)[J]. Journal of Central South University:Science and Technology,2018,49(7):39.)
[25]
吴胜利,刘宇,杜建新,等. 铁矿石的烧结基础特性之新概念[J]. 北京科技大学学报,2002,24(3):254.(WU Sheng-li,LIU Yu,DU Jian-xin,et al. New concept of iron ores sintering basic characteristics[J]. Journal of University of Science and Technology Beijing,2002,24(3):254.)
[26]
付忠旺,莫朝兴,陈小敏,等. 铁矿粉烧结液相流动性特征数的影响因素[J]. 钢铁,2018,53(12):18.(FU Zhong-wang,MO Chao-xing,CHEN Xiao-min,et al. Influence factors of fluidity characteristic number of iron ore powder[J]. Iron and Steel,2018,53(12):18.)
[27]
WU S L,ZHANG G L,CHEN S G,et al. Influencing factors and effects of assimilation characteristic of iron ores in sintering process[J]. ISIJ International,2014,54(3):582.
[28]
谢运强,张中中,王子宏,等. 某钢铁企业常用铁矿粉烧结基础性能及优化配矿[J]. 中国冶金,2018,28(3):9.(XIE Yun-qiang,ZHANG Zhong-zhong,WANG Zi-hong,et al. Sintering basic characteristics of iron ores used in an iron and steel plant and optimum proportioning ores[J]. China Metallurgy,2018,28(3):9.)
[29]
朱德庆,薛钰霄,潘建,等. 铁矿粉高温反应性能综合指数评价烧结性能[J]. 钢铁,2017,52(8):19.(ZHU De-qing,XUE Yu-xiao,PAN Jian,et al. Evaluation of sintering behaviors with comprehensive index of high temperature reaction properties of iron ore fines[J]. Iron and Steel,2017,52(8):19.)
[27]
WU S L,ZHANG G L,CHEN S G,et al. Influencing factors and effects of assimilation characteristic of iron ores in sintering process[J]. ISIJ International,2014,54(3):582.
[28]
谢运强,张中中,王子宏,等. 某钢铁企业常用铁矿粉烧结基础性能及优化配矿[J]. 中国冶金,2018,28(3):9.(XIE Yun-qiang,ZHANG Zhong-zhong,WANG Zi-hong,et al. Sintering basic characteristics of iron ores used in an iron and steel plant and optimum proportioning ores[J]. China Metallurgy,2018,28(3):9.)
[29]
朱德庆,薛钰霄,潘建,等. 铁矿粉高温反应性能综合指数评价烧结性能[J]. 钢铁,2017,52(8):19.(ZHU De-qing,XUE Yu-xiao,PAN Jian,et al. Evaluation of sintering behaviors with comprehensive index of high temperature reaction properties of iron ore fines[J]. Iron and Steel,2017,52(8):19.)