Effects of Heat Treatment on Nitrided Layer of H13 Tool Steel
LIN Gaoyong1,2,ZHENG Xiaoyan1,FENG Di1,YANG Wei1,ZHANG Shenghua1,2
1School of Material Science and Engineering, Changsha 410083, Hunan, China;2The Key Laboratory of Nonferrous Metal Materials Science and Engineering, Ministry of Education, Center South University, Changsha 410083, Hunan, China
Abstract：The microstructure and hardness of the layer of H13 tool steel gasnitrided in different heat treatment conditions were studied by Xray, SEM and microhardness test. The results show that, the thickness of nitrided layer was 0.24 mm with a compound layer 10 μm, surface hardness was HV950（HRC67）, for the specimen,which was nitrided after “quenching and twice tempering” and “quenching and threetime tempering”. The compound layer mainly consisted of εphase（Fe2N）, γ′phase and Fe3O4, and diffusion layer consisted αFe、εphase（Fe3N）, γ′phase and CrN. However, the specimen nitrided after “quenching” and “quenching and once tempering” couldn’t have a nitrided layer of comprehensive properties.
林高用;郑小燕;冯迪;杨伟;张胜华;. 热处理状态对H13模具钢渗氮层的影响[J]. 钢铁, 2008, 43(12): 63-0.
LIN Gaoyong;ZHENG Xiaoyan;FENG Di;YANG Wei;ZHANG Shenghua;. Effects of Heat Treatment on Nitrided Layer of H13 Tool Steel. Iron and Steel, 2008, 43(12): 63-0.
2008, Vol. 43 