高纯净GCr15轴承钢组织演变与快速球化工艺的研究
闫文凯 杨卯生 等
钢铁研究总院结构材料研究所
Microstructure evolution and rapid spheroidizing technology of high-purity of GCr15 bearing steel
摘要 摘要:本文研究了高纯净GCr15轴承钢预备组织与退火工艺对碳化物球化质量的影响;利用碳化物的金相形貌、数量、大小、分布及圆整度表征试验钢的球化质量。实验表明,优良的预备组织适宜的退火制度有利于碳化物在短时间内球化和细化,采用文中退火制度c,GCr15轴承钢圆整度为0.087、平均粒径为0.27μm,球化时间比传统工艺减少3.5h。
Abstract :Abstract:The paper studies that both the high-purity of GCr15 Bearing Steel tissue preparation and annealing process have an effect on carbide spheroidizing quality. it can get spherodization by carbide metallographic morphology,number,size,distribution and the roundness characteristics of the carbide quality. Using annealing schedule c of this paper, the GCr15 Bearing Steel roundness of 0.087, with an average particle size of 0.27μm, the spherodization of time shorter than the traditional process 3.5 hours
收稿日期: 2010-01-26
[1]
Jun Zhao, Hai-bin Zuo, Chao Ling, Wen-tao Guo, Jing-song Wang, Qing-guo Xue. Microstructure evolution of coke under CO2 and H2 O atmospheres [J]. 钢铁研究学报(英文版), 2020, 27(7): 743-754.
[2]
Sheng-li Wu, Xiao-bo Zhai, Li-xin Su, Xu-dong Ma. Ore-blending optimization for Canadian iron concentrate during iron ore sintering based on high-temperature characteristics of fines and nuclei [J]. 钢铁研究学报(英文版), 2020, 27(7): 755-769.
[3]
Feng Zhang, De-qing Zhu, Jian Pan, Zheng-qi Guo, Meng-jie Xu. Improving roasting performance and consolidation of pellets made of ultrafine and super high grade magnetite concentrates by modifying basicity [J]. 钢铁研究学报(英文版), 2020, 27(7): 770-781.
[4]
Da‑peng Li, Hua‑zhang Wu, Hai‑feng Wang, Hong Li. Growth of solidified shell in bloom continuous casting mold of hypo-peritectic steel based on a FeS tracer method [J]. 钢铁研究学报(英文版), 2020, 27(7): 782-787.
[5]
Jie Yang, Deng‑fu Chen, Miao‑yong Zhu. Crystallization and heat transfer of CaO–SiO2 -based slag for high-Mn–high-Al steel [J]. 钢铁研究学报(英文版), 2020, 27(7): 788-795.
[6]
Ping‑guo Jiang, Jin‑sheng Liu, Yi‑yu Xiao, Xiao‑heng Tan, Wen‑jie Liu. Recovery of iron from copper slag via modified roasting in CO–CO2 mixed gas and magnetic separation [J]. 钢铁研究学报(英文版), 2020, 27(7): 796-806.
[7]
Hai Wang, Dong Liu, Jian‑guo Wang, Hai‑ping Wang, Yang Hu, Hao‑dong Rao. Characterization of hot deformation behavior of 30Si2MnCrMoVE low-alloying ultra-high-strength steel by constitutive equations and processing maps [J]. 钢铁研究学报(英文版), 2020, 27(7): 807-819.
[8]
Chen Dong, Zheng‑dong Liu, Zheng‑zong Chen, Zhen Liu, Jia‑zhuang Zheng, Xi‑tao Wang. Hot deformation behavior of a heat-resistant alloy without γ′-phase [J]. 钢铁研究学报(英文版), 2020, 27(7): 820-833.
[9]
Jia‑jia Qiu, Min Zhang, Gu‑hui Gao, Zhun‑li Tan, Bing‑zhe Bai. Research and modeling on correlation among microstructure, yield strength and process of bainite/martensite steel [J]. 钢铁研究学报(英文版), 2020, 27(7): 834-841.
[10]
Xiao‑hui Chen, Bo Chen, Xu Cheng, Guo‑chao Li, Zheng Huang. Microstructure and properties of hybrid additive manufacturing 316L component by directed energy deposition and laser remelting [J]. 钢铁研究学报(英文版), 2020, 27(7): 842-848.
[11]
Huan Lin, Mao‑sheng Yang, Bai‑po Shu. Fretting wear behaviour of high-nitrogen stainless bearing steel under lubrication condition [J]. 钢铁研究学报(英文版), 2020, 27(7): 849-866.
[12]
Rui‑wu Li, Zheng Zhang, Jian‑wei Li, Ke‑xin Ma, Yuan‑yuan Guo, Yan‑wen Zhou, Fa‑yu Wu. Surface modification of 316L stainless steel by diamond-like carbon films [J]. 钢铁研究学报(英文版), 2020, 27(7): 867-874.
[13]
He‑ping Li, Sheng‑li Wu, Zhi‑bin Hong, Heng Zhou, Ming‑yin Kou. Development and application of coke oven gas spraying on sinter bed [J]. 钢铁研究学报(英文版), 2020, 27(6): 617-623.
[14]
Xin Jiang, Huai‑yu Zhang, Hai‑yan Zheng, Qiang‑jian Gao, Feng‑man Shen. Three-segment control theory of MgO/Al2 O3 ratio based on viscosity experiments and phase diagram analyses at 1500 °C [J]. 钢铁研究学报(英文版), 2020, 27(6): 624-630.
[15]
Qing‑song Zhang, Yi Min, Jiu‑jian Xu, Cheng‑jun Liu. Formation and evolution behavior of inclusions in Al-killed resulfurized free-cutting steel with magnesium treatment [J]. 钢铁研究学报(英文版), 2020, 27(6): 631-642.