Q345B结构钢的热压缩变形行为及流变应力模型
董方,宿成,张寄东
内蒙古科技大学材料与冶金学院， 内蒙古 包头 014010
Hot Compression Deformation Behavior and Rheological Model of Flow Stress of Q345B Structural Steel
DONG Fang,SU Cheng,ZHANG Ji-dong
School of Material and Metallurgy, Inner Mongolia University of Science and Technology, Baotou 014010, Nei Monggol, China
摘要 利用Gleeble-1500D热模拟试验机对钒、钛、铌微合金化Q345B低合金高强度结构钢（HSLA）进行了高温单道次压缩试验。测量了不同变形温度和变形速率下该钢的变形行为，分析了各变形参数对该钢动态再结晶和变形抗力的影响，得出动态再结晶激活能为451.47kJ/mol。并且建立了高温变形抗力的分段函数流变模型，该模型计算结果与试验值吻合较好。
Abstract ：The high tempeture single-pass compression experiment was carried out with Gleeble-1500D thermal simulator for V-Ti-Nb microalloyed Q345B steel (HSLA). The deformation behaviors of this steel was measured under different deformation temperatures and deformation rates, and the influence of process parameters on the dynamic recrystallization and deformation resistance was investigated. The value of Qdef was 451.47kJ/mol. The rheological model of segmented function of high temperature deformation resistance was established. The calculated results by the rheological model were in good agreement with experiments.
收稿日期: 2010-09-14
出版日期: 2011-10-09
[1]
Jun Zhao, Hai-bin Zuo, Chao Ling, Wen-tao Guo, Jing-song Wang, Qing-guo Xue. Microstructure evolution of coke under CO2 and H2 O atmospheres
[2]
Sheng-li Wu, Xiao-bo Zhai, Li-xin Su, Xu-dong Ma. Ore-blending optimization for Canadian iron concentrate during iron ore sintering based on high-temperature characteristics of fines and nuclei
[3]
Feng Zhang, De-qing Zhu, Jian Pan, Zheng-qi Guo, Meng-jie Xu. Improving roasting performance and consolidation of pellets made of ultrafine and super high grade magnetite concentrates by modifying basicity
[4]
Da‑peng Li, Hua‑zhang Wu, Hai‑feng Wang, Hong Li. Growth of solidified shell in bloom continuous casting mold of hypo-peritectic steel based on a FeS tracer method
[5]
Jie Yang, Deng‑fu Chen, Miao‑yong Zhu. Crystallization and heat transfer of CaO–SiO2 -based slag for high-Mn–high-Al steel
[6]
Ping‑guo Jiang, Jin‑sheng Liu, Yi‑yu Xiao, Xiao‑heng Tan, Wen‑jie Liu. Recovery of iron from copper slag via modified roasting in CO–CO2 mixed gas and magnetic separation
[7]
Hai Wang, Dong Liu, Jian‑guo Wang, Hai‑ping Wang, Yang Hu, Hao‑dong Rao. Characterization of hot deformation behavior of 30Si2MnCrMoVE low-alloying ultra-high-strength steel by constitutive equations and processing maps
[8]
Chen Dong, Zheng‑dong Liu, Zheng‑zong Chen, Zhen Liu, Jia‑zhuang Zheng, Xi‑tao Wang. Hot deformation behavior of a heat-resistant alloy without γ′-phase
[9]
Jia‑jia Qiu, Min Zhang, Gu‑hui Gao, Zhun‑li Tan, Bing‑zhe Bai. Research and modeling on correlation among microstructure, yield strength and process of bainite/martensite steel
[10]
Xiao‑hui Chen, Bo Chen, Xu Cheng, Guo‑chao Li, Zheng Huang. Microstructure and properties of hybrid additive manufacturing 316L component by directed energy deposition and laser remelting
[11]
Huan Lin, Mao‑sheng Yang, Bai‑po Shu. Fretting wear behaviour of high-nitrogen stainless bearing steel under lubrication condition
[12]
Rui‑wu Li, Zheng Zhang, Jian‑wei Li, Ke‑xin Ma, Yuan‑yuan Guo, Yan‑wen Zhou, Fa‑yu Wu. Surface modification of 316L stainless steel by diamond-like carbon films
[13]
He‑ping Li, Sheng‑li Wu, Zhi‑bin Hong, Heng Zhou, Ming‑yin Kou. Development and application of coke oven gas spraying on sinter bed
[14]
Xin Jiang, Huai‑yu Zhang, Hai‑yan Zheng, Qiang‑jian Gao, Feng‑man Shen. Three-segment control theory of MgO/Al2 O3 ratio based on viscosity experiments and phase diagram analyses at 1500 °C
[15]
Qing‑song Zhang, Yi Min, Jiu‑jian Xu, Cheng‑jun Liu. Formation and evolution behavior of inclusions in Al-killed resulfurized free-cutting steel with magnesium treatment
2011, Vol. 46 