Abstract:The energy-saving potential for different low carbon ironmaking approaches was investigated facing to the given conditions of materials. The result shows that for the general BF, when the indirect reduction approaches to the chemical balance, the gas utilization can reach up to 56.99% and fuel ratio is decreased by 28.37kg/t. For oxygen blast furnace, when the top gas is totally recycled the fuel ratio can be reduced to 385.6kg/t. The fuel ratio can also be reduced through the injection of coke oven gas. About 5.0kg/t coke ratio can be saved by every 10m3 COG injection. Along with the oxygen enrichment being improved, the optimal injection volume corresponding to the minimal fuel ratio increases and as a result the lowest fuel ratio decreases. When the oxygen enrichment is 6%-8% and injection volume is 160-180m3/t. the coke ratio can be reduced maximally by 53-54kg/t. Using high reactivity coke in blast furnace can decrease temperature of thermal reservation zone and the balance concentration of CO decreases accordingly. When the balance concentration of CO is decreased by the step of 2.5% from 70%-60%, the fuel ratio can be reduced by 10.30-12.20kg/t theoretically and the reducing rate decreases.
收稿日期: 2012-05-02
出版日期: 2013-01-14
引用本文:
左海滨,张建良,王筱留. 高炉低碳炼铁分析[J]. 钢铁, 2012, 47(12): 86-94.
ZUO Hai-bin,ZHANG Jian-liang,WANG Xiao-liu. Analysis on Low Carbon Iron-Making for BF. Iron and Steel, 2012, 47(12): 86-94.
Tatsuro ARIYAMA, Michitaka SATO. Optimization of Ironmaking Process for Reducing CO2 Emissions in the Integrated Steel Works. ISIJ International, 2006, 46(12):1736.
[3]
Tatsuro ARIYAMA, Michitaka SATO. Optimization of Ironmaking Process for Reducing CO2 Emissions in the Integrated Steel Works. ISIJ International, 2006, 46(12):1736.
[4]
Guangqing Zuo, Alexandra Hirsch. The Trial of the Top Gas Recycling Blast Furnace at LKAB and Scale-up[C]. Proceedings of the 4th Ulcos seminar, 2008.
[4]
Guangqing Zuo, Alexandra Hirsch. The Trial of the Top Gas Recycling Blast Furnace at LKAB and Scale-up[C]. Proceedings of the 4th Ulcos seminar, 2008.
[5]
齐渊洪,严定鎏,高建军等. 氧气高炉工业化试验研究[J]. 钢铁,2011,46(3):7.
[5]
齐渊洪,严定鎏,高建军等. 氧气高炉工业化试验研究[J]. 钢铁,2011,46(3):7.
[6]
Peter Diemer,Hans-Jürgen Killich,Klaus Knop,et al.Potentials for Utilization of Coke Oven Gas in Integrated Iron and Steel Works[J].Stahl und Eisen,2004,124 (7):21.
[6]
Peter Diemer,Hans-Jürgen Killich,Klaus Knop,et al.Potentials for Utilization of Coke Oven Gas in Integrated Iron and Steel Works[J].Stahl und Eisen,2004,124 (7):21.