Development of Hot Rolling Plate Q450NQR1 With High Corrosion Resistant for Railway Boxcar
LU Jun-hui1,WANG Xiao-chun2,LIU Jia-qi1,ZHANG Cheng-wu2,ZHANG Hui1,PIAO Feng-yun2
1. State Key Laboratory of Advanced Steel Processing and Products, Central Iron and Steel Research Institute, Beijing 100081, China 2. Technology Center, Tonghua Iron and Steel Group Co., Ltd., Tonghua 134000, Jilin, China
Abstract：The hot rolling plate Q450NQR1 with high corrosion resistant for railway boxcar was developed by hot metal pre-treatment—120t top and bottom combined blown converter—LF refining—FTSC continuous casting machine—2R—5F mill—coiling with TMCP process. The results show that the microstructure of plate is ferrite-pearlite and grain size rating is 12, the yield strength and tensile strength are 509.2MPa and 580MPa, respectively. The impact absorbing energy at －40℃ is about 170J, and corrosion resistant is very good, and the corrosion rate for 144h is decreased 33.33% compared with the Q345B. The production can meet the requirement of railway boxcar.
卢军辉，王晓春，刘家琪，张成武，张慧，朴峰云. 高耐候性Q450NQR1货车车厢板的开发[J]. 钢铁, 2013, 48(2): 75-79.
LU Jun-hui,WANG Xiao-chun,LIU Jia-qi,ZHANG Cheng-wu,ZHANG Hui,PIAO Feng-yun. Development of Hot Rolling Plate Q450NQR1 With High Corrosion Resistant for Railway Boxcar. Iron and Steel, 2013, 48(2): 75-79.
H.E. Townsend. Effects of alloying elements on the corrosion of steel in industrial atmospheres[J].Corrosion,2001,57(6):497-501
[4]
H.E. Townsend. Effects of alloying elements on the corrosion of steel in industrial atmospheres[J].Corrosion,2001,57(6):497-501
[5]
Yamashita M,Nagano H,Misawa T,et al.Structure of protective rust layers formed on weathering steels by long- term exposure in the industrial atmospheres of Japan and North America[J].ISIJ International,1998,38(3):285-290
[5]
Yamashita M,Nagano H,Misawa T,et al.Structure of protective rust layers formed on weathering steels by long- term exposure in the industrial atmospheres of Japan and North America[J].ISIJ International,1998,38(3):285-290
[6]
Chiaki OUCHI,Tetsuya SAMPEI,Isao KOZASU.The Effect of Hot Rolling Condition and Chemical Composition on the Onset Temperature of Gamma-Alpha Transformation after Hot Rolling [J].Transactions of the ISIJ,1982,22(3):214-222
[6]
Chiaki OUCHI,Tetsuya SAMPEI,Isao KOZASU.The Effect of Hot Rolling Condition and Chemical Composition on the Onset Temperature of Gamma-Alpha Transformation after Hot Rolling [J].Transactions of the ISIJ,1982,22(3):214-222
2013, Vol. 48 