1. Materials and Metallurgy School, UST Inner Mongolia, Baotou 014010, Nei Mongol, China 2. Research Institute, Wuhan Iron and Steel Group Corp., Wuhan 430080, Hubei, China
Abstract:The effects of cooling process after rolling on microstructure, precipitated phase and mechanical properties of low-carbon bainite steel were investigated by method of SEM and TEM. The results show that ferrite and bainite dual phases can be obtained with air-cooling and accelerated cooling process after hot-rolled. The percentage of ferrite phase increases with the end of air-cooling temperature reduced, the size of ferrite and precipitated phase is larger, the lath of bainite is sharper and the edge is clearer. The shape of M/A constituent is film-like and changes with temperature. When temperature of completion in air-cooling are between 725℃ and 740℃, then it is cooled to 440℃ with cooling rate of 15℃/s, the comprehensive mechanical properties are excellent and can reach the requirements of Q690 of GB/T1591.
李德发 ,王世森,熊玉彰,邢淑清,熊涛,余宏伟. 轧后冷却工艺对铌钛微合金化低碳贝氏体钢组织性能的影响[J]. 钢铁, 2013, 48(3): 71-75.
Low-Carbon Bainite SteelLI De-fa,,WANG Shi-sen,XIONG Yu-zhang,XING Shu-qing,XIONG Tao,YU Hong-wei. Effect of Cooling Process After Rolling on Microstructure and Mechanical Property of Nb-Ti Microalloyed. Iron and Steel, 2013, 48(3): 71-75.