Secondary Cooling System for 37Mn2 Steel With Round Continuous Caster
LI Jian-quan1 ,CHEN Deng-fu2, WU Guo-rong3, LEI Yang-wei1
1. Panzhihua Steel and Vanadium Co., Ltd., Pangang Group, Panzhihua 617062, Sichuan, China 2. College of Materials Science and Engineering, Chongqing University, Chongqing 400030, China 3. Pangang Group Research Institute Co., Ltd., Panzhihua 617000, Sichuan, China
Abstract：Base on the high temperature mechanics performance and metallurgical criterion, heat transfer mathematical model was proposed, and the round billet temperature and thickness of solidified shell were calculated with the model. According to the calculation results, the model was optimized. And on this basis, the reasonable secondary cooling system was proposed. The secondary cooling system for 37Mn2 steel with round continuous caster was studied, and the secondary cooling system which was matched with the continuous casting process and equipments was established and it was applied in industrial production. The results show that there is no difference between the measurement and calculated results in round billet temperature. The surface temperature in straightening zone is above 950℃. The internal quality of round billet is perfect and the level of central crack and porosity is 0, and the level of shrinkage, center porosity and center segregation is below 1.5. The quality of round billet can meet the needs of subsequent production.
黎建全， 陈登福 吴国荣 雷阳伟. 37Mn2钢连铸圆坯的二次冷却制度[J]. 钢铁, 2014, 49(1): 45-51.
LI Jian-quan ,CHEN Deng-fu, WU Guo-rong, LEI Yang-wei. Secondary Cooling System for 37Mn2 Steel With Round Continuous Caster. Iron and Steel, 2014, 49(1): 45-51.
B G Thomas. Continuous Casting [M]. Elsevier Science Ltd, Oxford, UK, 2001 (2):1595-1599.
[1]
B G Thomas. Continuous Casting [M]. Elsevier Science Ltd, Oxford, UK, 2001 (2):1595-1599.
[2]
F. Weinberg. The Casting of Steel [J]. Metallurgical and Materials Transactions A, 1975, 6(11):1971-1985.
[2]
F. Weinberg. The Casting of Steel [J]. Metallurgical and Materials Transactions A, 1975, 6(11):1971-1985.
[3]
T. Techima, J. Kubota, M. Suzuki, et al. Influence of Casting Conditions on Molten Steel Flow in Continuous Casting Mold at High Speed Casting of Slabs[J]. Tetsu-to-Hagane, 1993, 79(5):576-584.
[4]
张富强, 王久彬.连铸二次冷却的优化和控制[J]. 鞍钢技术, 1999(1):54-58.
[3]
T. Techima, J. Kubota, M. Suzuki, et al. Influence of Casting Conditions on Molten Steel Flow in Continuous Casting Mold at High Speed Casting of Slabs[J]. Tetsu-to-Hagane, 1993, 79(5):576-584.
[4]
张富强, 王久彬.连铸二次冷却的优化和控制[J]. 鞍钢技术, 1999(1):54-58.
[5]
蔡开科. 连续铸钢原理与工艺[M]. 北京: 冶金工业出版社, 1994.
[5]
蔡开科. 连续铸钢原理与工艺[M]. 北京: 冶金工业出版社, 1994.
[6]
陈登福; 颜广庭;连铸二冷区的夹辊与铸坯间传热研究[J]. 炼钢1991.(1):39-43.
[6]
陈登福; 颜广庭;连铸二冷区的夹辊与铸坯间传热研究[J]. 炼钢1991.(1):39-43.
[7]
G VanDrunen, JK Brimacombe.Internal Cracks in Strand Cast Billets[J]. Ironmaking and Steelmaking, 2(2): 125-133.
[7]
G VanDrunen, JK Brimacombe.Internal Cracks in Strand Cast Billets[J]. Ironmaking and Steelmaking, 2(2): 125-133.
2014, Vol. 49 