Effect of Composition and Heat Treatment on Microstructure and Mechanical and Magnetic Property of 403 Steel for Rotator
SUN Yong-qing1,LIANG Jian-xiong1,SUN Guo-qiang2, YANG Zhi-yong1,LI Wen-hui1,ZHANG Li-na3
1. Special Steel Institute, Central Iron and Steel Research Institute, Beijing 100081, China 2. Kunming University of Science and Technology,Kunming 650093,Yunnan, China 3. Fushun Special Steel Co., Ltd., Fushun 113001, Liaoning, China
Abstract:Three 403 steel bars of different compositions were searched, which were produced by 200kg VIM furnace and forged into 120mm. Mechanical and magnetic properties were tested after heat treatment 950-1000℃×1h OC+720-750℃×3h OC. The results show that, 403 steel bar with higher Ni or N has higher strength, magnetoconductivity and toughness especially. Compared with test steel bar with higer Ni, bar with higher N has higher magnetic induction in lower magnetic field intensity, while lower magnetic induction in higher magnetic field intensity. Strengthening mechanism was searched and the conclusion can be made to guide the production of this type steel for rotator.
孙永庆 梁剑雄 孙国强 杨志勇 李文辉 张丽娜. 化学成分和热处理工艺对转子用403不锈钢组织和性能的影响[J]. 钢铁, 2014, 49(1): 66-69.
SUN Yong-qing,LIANG Jian-xiong,SUN Guo-qiang, YANG Zhi-yong,LI Wen-hui,ZHANG Li-na. Effect of Composition and Heat Treatment on Microstructure and Mechanical and Magnetic Property of 403 Steel for Rotator. Iron and Steel, 2014, 49(1): 66-69.