Effect of Heat Treatment on Mechanical Properties and Corrosion Resistance of 15-5PH Stainless Steel
ZHANG Xiu-li1, CHEN Ming-xin2, LIU Zhen-bao2, LIANG Jian-xiong2, YANG Zhi-yong2, YU Qiang2
1. Technical Centre, Fushun Special Steel Group Co., Ltd., Fushun 113001, Liaoning, China 2. Central Iron and Steel Research Institute, Beijing 100081, China
Abstract:This paper studies the effect of heat treatment on mechanical properties and corrosion resistance of 15-5PH precipitation hardening stainless steel, and observes the precipitated phase in steel.The results show that the strength of steel decreased with the aging temperature increased and the aging time extended, while the toughness of steel increased. This is caused by the reverse austenite volume fraction increased with the temperature raised; The pitting corrosion resistance of the steel reduced along with the aging temperature increased, the corrosion resistance of steel was at the poorest when aging at 580 and 600 ℃, while the corrosion resistance of steel reached the best and the strength was the highest when aging at 480 ℃, and the main precipitated phase was a rich copper phase of face-centered cubic structure in steel.
Habibi Bajguirani H.R..The effect of ageing upon the microstructure and mechanical properties of type 15-5PH stainless steel[J].Material Science and Engineering, 2002, (A338): 142~ 159.
[6]
Habibi Bajguirani H.R..The effect of ageing upon the microstructure and mechanical properties of type 15-5PH stainless steel[J].Material Science and Engineering, 2002, (A338): 142~ 159.
[7]
Akitsugu FUJITA,Takayuki KAWANO,Hidetoshi SUEOKA,Fumikazu SAKAI. Heat Treatment of Weld Part in 15-5PH Stainless Steel and Manufacturing of Actual Hydrofoil for High Speed Passenger Craft[J],ISIJ International,1998,38(8):866-874.
[7]
Akitsugu FUJITA,Takayuki KAWANO,Hidetoshi SUEOKA,Fumikazu SAKAI. Heat Treatment of Weld Part in 15-5PH Stainless Steel and Manufacturing of Actual Hydrofoil for High Speed Passenger Craft[J],ISIJ International,1998,38(8):866-874.
[8]
T. Wu, M. Coret , A. Combescure.Numerical simulation of welding induced damage and residual stress of martensitic steel 15-5PH [J], International Journal of Solids and Structures 2008,45: 4973–4989.
[8]
T. Wu, M. Coret , A. Combescure.Numerical simulation of welding induced damage and residual stress of martensitic steel 15-5PH [J], International Journal of Solids and Structures 2008,45: 4973–4989.
[9]
Chasse K.R, Singh P.M.Effect of microstructural anisotropy on stress corrosion cracking of hot rolled duplex stainless steels[J], Corrosion Engineering, Science and Technology, 2012,47( 3):170-176.
[9]
Chasse K.R, Singh P.M.Effect of microstructural anisotropy on stress corrosion cracking of hot rolled duplex stainless steels[J], Corrosion Engineering, Science and Technology, 2012,47( 3):170-176.
[10]
HAYNE M.L, ANDERSON P.I, FINDLEY K.O,and VANTYNE C.J.Effect of Microstructural Banding on the Fatigue Behavior of Induction-Hardened 4140 Steel[J],METALLURGICAL AND MATERIALS TRANSACTIONS A, 2013,44A(8),3428-3433.
[10]
HAYNE M.L, ANDERSON P.I, FINDLEY K.O,and VANTYNE C.J.Effect of Microstructural Banding on the Fatigue Behavior of Induction-Hardened 4140 Steel[J],METALLURGICAL AND MATERIALS TRANSACTIONS A, 2013,44A(8),3428-3433.
[11]
Y.Yang,H.tan, Z.Zhang, Z.Wang, Y,Jiang,L.Jiang,J.Li.]Effect of Annealing Temperature on the Pitting Corrosion Behavior of UNS S82441 Duplex Stainless Steel,Corrosion Science Section, 2013, 69 (2):167-173.
[11]
Y.Yang,H.tan, Z.Zhang, Z.Wang, Y,Jiang,L.Jiang,J.Li.]Effect of Annealing Temperature on the Pitting Corrosion Behavior of UNS S82441 Duplex Stainless Steel,Corrosion Science Section, 2013, 69 (2):167-173.