Abstract：In certain conditions of dephosphorization agent type and proportion, with the help of micro sintering experiment method, the basicity, temperature, carbon and phosphorus content on the influence of gasification dephosphorization rate of high phosphorus steel slag was studied. The studies have shown that increasing the alkalinity, gasification dephosphorization rate of steel slag decreased, improving the temperature, gasification dephosphorization rate rose, with the increased amount of carbon in steel slag, the rate of gasification dephosphorization first increased and then reduced, increasing the phosphorus content, gasification dephosphorization rate increased，and when the phosphorus content reached a certain level, the effect of phosphorus content on the gasification dephosphorization rate was weakened, and ultimately determine the optimum state of each factor.
张 伟， 刘卫星， 李 杰， 李运刚， 邢宏伟. 高磷钢渣气化脱磷影响因素的实验[J]. 钢铁, 2015, 50(1): 11-14.
ZHANG Wei, LIU Wei-xing, LI Jie, LI Yun-gang, XING Hong-wei. Main factors of gasification dephosphorization of high phosphorus steel slag. Iron and Steel, 2015, 50(1): 11-14.
Fukagai S, Hamano T and Tsukihashi F. Formation Reaction of Phosphate Compound on Multi Phase Flux at 1573K[J]. ISIJ International, 2007, 47(1): 187-189.
[9]
Fukagai S, Hamano T and Tsukihashi F. Formation Reaction of Phosphate Compound on Multi Phase Flux at 1573K[J]. ISIJ International, 2007, 47(1): 187-189.
[10]
Suito H, Inoue R. Behavior of phosphorous transfer from CaO-FetO-P2O5(-SiO2) slag to CaO particles[J]. ISIJ lntemational, 2006, 46(2): 180-187.
[10]
Suito H, Inoue R. Behavior of phosphorous transfer from CaO-FetO-P2O5(-SiO2) slag to CaO particles[J]. ISIJ lntemational, 2006, 46(2): 180-187.
[11]
陈伟. 转炉钢渣的处理和利用[J]. 湖南有色金属, 2000, 16(4):36-37.
[11]
陈伟. 转炉钢渣的处理和利用[J]. 湖南有色金属, 2000, 16(4):36-37.
[12]
B Deo, J Halder, B Snoeijer, et al. Effect of MgO and Al2O3 variations in oxygen steelmaking (BOF) slag on slag morphology and phosphorus distribution[J]. Ironmaking and Steelmaking, 2005, 32(1):54-60.
[12]
B Deo, J Halder, B Snoeijer, et al. Effect of MgO and Al2O3 variations in oxygen steelmaking (BOF) slag on slag morphology and phosphorus distribution[J]. Ironmaking and Steelmaking, 2005, 32(1):54-60.
Morita K, Guo M, Oka N, et al. Resurrection of iron and phosphorus resource in steelmaking slags[J]. Journal of Material Cycles and Waste Management, 2002(4):93-101.
[15]
Morita K, Guo M, Oka N, et al. Resurrection of iron and phosphorus resource in steelmaking slags[J]. Journal of Material Cycles and Waste Management, 2002(4):93-101.
2015, Vol. 50 