Abstract:Large amount of iron-bearing dust could be generated in the steel production process. At present,the best way of effective utilization of iron-bearing dust in China is pelletizing using the dust and to producemetallized pellet using the rotary hearth furnace. The basic characteristics of iron-bearing dust,including sintering,blast furnace and electric furnace dust,are investigated through the chemical analysis,laser particle size,BET specific surface area and X-ray diffraction. Furthermore,the pelletizing experiment ofthree kinds of dust is carried out,and the optimal pelletizing parameters are investigated based on the balling dynamics and the green pellet strength. The results show that the dust from sintering has good forming dynamics,while its green pellet strength can not meet the requirement under the current experimental condition. The dust from electric furnace has a relative large adhension,hence,tends to stick on the wall. The dust from blast furnace has not only a good forming dynamics,but has a large green pellet strengh. To ensure the yield and quality of the pellet,the appropriate pelletizing parameters of BFD are 12.5%~13.0%moisture,2% bentonite,20 min pelletizing time,27~31 r/min rotating speed and 5 kg feeding amount.
收稿日期: 2016-07-19
出版日期: 2017-05-04
引用本文:
鲁 华,吴胜利,张建良,常 凤,李 宏. 钢厂含铁粉尘动力学成球性能[J]. 钢铁, 2017, 52(5): 5-12.
LU Hua,WU Sheng-li,ZHANG Jian-liang,CHANG Feng,LI Hong. Forming dynamics of pellet made frozinc-bearing dust in steel plant. Iron and Steel, 2017, 52(5): 5-12.
张建良, 闫永芳, 徐萌, 等. 高炉含锌粉尘的脱锌处理[J]. 钢铁, 2006, 41(10): 78.ZHANG Jian-liang, YAN Yong-fang, XU Meng, et al. Research on Removal of Zn From Blast Furnace Dust[J]. Iron and Steel, 2006, 41(10): 78.
[2]
张建良, 闫永芳, 徐萌, 等. 高炉含锌粉尘的脱锌处理[J]. 钢铁, 2006, 41(10): 78.ZHANG Jian-liang, YAN Yong-fang, XU Meng, et al. Research on Removal of Zn From Blast Furnace Dust[J]. Iron and Steel, 2006, 41(10): 78.
[3]
Kelebek. S, Yuk. S, Davis. B. Characterization of basic oxygen furnace dust and zinc removal[J]. Minerals Engineering, 2004 (17): 285?291.
[3]
Kelebek. S, Yuk. S, Davis. B. Characterization of basic oxygen furnace dust and zinc removal[J]. Minerals Engineering, 2004 (17): 285?291.
[4]
胡晓军, 郭婷, 周国治, 等. 含锌冶金粉尘处理技术的发展和现状[J]. 钢铁研究学报, 2011, 23(7): 1.HU Xiao-jun, GUO Ting, ZHOU Guo-zhi, et al. Development and Current States of Techniques of Disposal Zinc-Containing Dust in Metallurgical Industry[J]. Journal of Iron and Steel Research, 2011, 23(7): 1.
[4]
胡晓军, 郭婷, 周国治, 等. 含锌冶金粉尘处理技术的发展和现状[J]. 钢铁研究学报, 2011, 23(7): 1.HU Xiao-jun, GUO Ting, ZHOU Guo-zhi, et al. Development and Current States of Techniques of Disposal Zinc-Containing Dust in Metallurgical Industry[J]. Journal of Iron and Steel Research, 2011, 23(7): 1.
[5]
王静松, 杨慧贤, 佘雪峰, 等. 转底炉处理冶金粉尘工艺的锌钾钠脱除及烟气形成[J]. 重庆大学学报, 2011, 34(3): 82.WANG Jing-song, YANG Hui-xian, SHE Xue-feng, et al. Study on mechanism of Zn, K, Na removal and flue gas formation in RHF direct reduction treat metallurgical dust process[J]. Journal of Chongqing University, 2011, 34(3): 82.
[5]
王静松, 杨慧贤, 佘雪峰, 等. 转底炉处理冶金粉尘工艺的锌钾钠脱除及烟气形成[J]. 重庆大学学报, 2011, 34(3): 82.WANG Jing-song, YANG Hui-xian, SHE Xue-feng, et al. Study on mechanism of Zn, K, Na removal and flue gas formation in RHF direct reduction treat metallurgical dust process[J]. Journal of Chongqing University, 2011, 34(3): 82.
[6]
佘雪峰,薛庆国,董杰吉,等.钢铁厂典型粉尘的基本物性与利用途径分析.过程工程学报,2009,9(增刊): 7.SHE Xue-feng, XUE Qing-guo, DONG Jie-ji, et al. Study on Basic Properties of Typical Industrial Dust from Iron and Steel Plant and Analysis of Its Utilization[J]. The Chinese Journal of Process Engineering, 2009,9(S1): 7.
[6]
佘雪峰,薛庆国,董杰吉,等.钢铁厂典型粉尘的基本物性与利用途径分析.过程工程学报,2009,9(增刊): 7.SHE Xue-feng, XUE Qing-guo, DONG Jie-ji, et al. Study on Basic Properties of Typical Industrial Dust from Iron and Steel Plant and Analysis of Its Utilization[J]. The Chinese Journal of Process Engineering, 2009,9(S1): 7.
[7]
Machado. J.G.M.S, Brehm. F.A, Moraes. N. C.A.M, et al. Chemical, physical, structural and morphological characterization of the electric arc furnace dust[J]. Journal of Hazardous Materials, 2006, 136(3): 953.
[7]
Machado. J.G.M.S, Brehm. F.A, Moraes. N. C.A.M, et al. Chemical, physical, structural and morphological characterization of the electric arc furnace dust[J]. Journal of Hazardous Materials, 2006, 136(3): 953.
[8]
Silva. M.C, Bernardes. A.M, Bergmann. C.P, et al. Characterisation of electric arc furnace dust generated during plain carbon steel production[J]. Ironmaking and Steelmaking, 2008, 35(4): 315.
[8]
Silva. M.C, Bernardes. A.M, Bergmann. C.P, et al. Characterisation of electric arc furnace dust generated during plain carbon steel production[J]. Ironmaking and Steelmaking, 2008, 35(4): 315.
[9]
PENG Cui, GUO Zhan-cheng, ZHANG Fang-li, et al. Discovery of potassium chloride in the sintering dust by chemical and physical characterization[J]. ISIJ International, 2008, 48(10): 1398.
[9]
PENG Cui, GUO Zhan-cheng, ZHANG Fang-li, et al. Discovery of potassium chloride in the sintering dust by chemical and physical characterization[J]. ISIJ International, 2008, 48(10): 1398.
[10]
杜光宝, 张梅, 郭敏. 电炉粉尘中锌金属回收的试验研究[J]. 钢铁研究学报, 2010, 22(10): 25.DU Guang-bao, ZHANG Min, GUO Min. Experimental study on metallic zinc reclaiming from electric arc furnace dust[J]. Journal of Iron and Steel Research, 2010, 22(10): 25.
[10]
杜光宝, 张梅, 郭敏. 电炉粉尘中锌金属回收的试验研究[J]. 钢铁研究学报, 2010, 22(10): 25.DU Guang-bao, ZHANG Min, GUO Min. Experimental study on metallic zinc reclaiming from electric arc furnace dust[J]. Journal of Iron and Steel Research, 2010, 22(10): 25.
[11]
王东彦,陈伟庆,周荣章,等.钢铁厂含锌、铅粉尘基本物性及造球工艺[J].北京科技大学学报,1998,20(2): 113.WANG Dong-yan, CHEN Wei-qinbg, ZHOU Rong-zhang, et al. Basic properties and pellet making process for Iron and Steel plant Zn-Pb-bearing dust[J]. Univ Sci Technol Beijing, 1998, 20(2): 113.
[11]
王东彦,陈伟庆,周荣章,等.钢铁厂含锌、铅粉尘基本物性及造球工艺[J].北京科技大学学报,1998,20(2): 113.WANG Dong-yan, CHEN Wei-qinbg, ZHOU Rong-zhang, et al. Basic properties and pellet making process for Iron and Steel plant Zn-Pb-bearing dust[J]. Univ Sci Technol Beijing, 1998, 20(2): 113.
[12]
代书华, 刘百臣, 赵庆杰, 等. 含锌电炉粉尘的造球特性[J]. 材料与冶金学报, 2004, 3(3): 185.DAI Shu-hua, LIU Bai-chen, ZHAO Qing-jie, et al. Pelletizing properties of zinc-bearing EAF dust[J]. Journal of Materials and Metallurgy, 2004, 3(3): 185.
[12]
代书华, 刘百臣, 赵庆杰, 等. 含锌电炉粉尘的造球特性[J]. 材料与冶金学报, 2004, 3(3): 185.DAI Shu-hua, LIU Bai-chen, ZHAO Qing-jie, et al. Pelletizing properties of zinc-bearing EAF dust[J]. Journal of Materials and Metallurgy, 2004, 3(3): 185.
[13]
付守澄, 傅菊英. 铁精矿成球动力学研究[J]. 烧结球团, 1982, (5): 1.FU Shou-cheng, FU Ju-ying. Study on forming dynamics of pellet made from magnetite concentrate[J]. Sintering and Pelletizing, 1982, (5): 1.
[13]
付守澄, 傅菊英. 铁精矿成球动力学研究[J]. 烧结球团, 1982, (5): 1.FU Shou-cheng, FU Ju-ying. Study on forming dynamics of pellet made from magnetite concentrate[J]. Sintering and Pelletizing, 1982, (5): 1.
[14]
Takano. C, Mour?o. M.B. Self-reducing pellets for ironmaking: mechanical behavior[J]. Mineral Processing and Extractive Metallurgy Review, 2003, 24(3): 233.
[14]
Takano. C, Mour?o. M.B. Self-reducing pellets for ironmaking: mechanical behavior[J]. Mineral Processing and Extractive Metallurgy Review, 2003, 24(3): 233.
[15]
张家驹.铁冶金学.沈阳: 东北工学院出版社,1987Zhang Jia-ju. Iron and Steel metallurgy. Shenyang: House of northeast institute of technology Press, 1987
[15]
张家驹.铁冶金学.沈阳: 东北工学院出版社,1987Zhang Jia-ju. Iron and Steel metallurgy. Shenyang: House of northeast institute of technology Press, 1987