热镀锌双相钢表面粗糙问题分析与控制

doi:10.13228/j.boyuan.issn0449-749x.20160419

摘要
图/表
参考文献
相关文章 (0)

全文: PDF (0 KB) HTML (0 KB)
输出: BibTeX | EndNote (RIS)

摘要目前强度级别较高的双相钢产品已经可以普遍采用热镀锌工艺生产，热镀锌双相钢在生产过程中，表面出现明显的粗糙缺陷，形成边部与中部的色差，严重影响热镀锌双相钢产品表面质量。粗糙缺陷伴随粗糙度异常升高、锌层不均、抑制层形成不良、基板表面微裂纹等现象。分析认为，基板表面微裂纹是造成热镀锌双相钢表面粗糙的主要原因。热轧态组织和冷轧压下率是决定冷硬板浅表层微裂纹形成的关键因素。通过优化卷取温度及热轧卷厚度，改善热轧态组织及降低冷轧压下率，可有效控制冷轧板表面浅表层微裂纹的形成，从而良好解决热镀锌双相钢表面粗糙问题。

	服务

	把本文推荐给朋友
	加入我的书架
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	李研

关键词 ：热镀锌双相钢粗糙微裂纹卷取温度冷轧压下率

Abstract：Hot dip galvanized steel with high strength such as DP （dual phase） steel has been widely produced. During the galvanizing process of DP steel， coarse surface defect isfound on the surface of the zinc layer which causes severe colour difference between the edge and the middle of the strip. Coarse surface defect has very bad effect on the surface quality of the galvanized strip. The abnormal increasement of the roughness， the uneven zinc layer， the low-quality inhibition layer and the microcrack on the substrate surface are always in company with the coarse surface defect. The microcrack on the substrate surface is considered to be the main reason of the coarse surface defect of the DP steel. The microstructure of the hot rolled strip and the reduction ratio of the cold rolling process are the key factors to determine the microcrack on the substrate surface. The formation of the microcrack on the substrate surface can be eliminated by optimizing the microstructure of the hot rolled strip and reducing the reduction ratio of the cold rolling process and the coarse surface problem can be solved effectively.

收稿日期: 2016-09-14 出版日期: 2017-06-09

引用本文:

李研，张亮亮，于洋，刘鸿明，齐达，高小丽. 热镀锌双相钢表面粗糙问题分析与控制[J]. 钢铁, 2017, 52(6): 94-100. LI Yan，ZHANG Liang-liang，YU Yang，LIU Hong-ming，QI Da，GAO Xiao-li. Analysis and control of coarse surface of galvanized dual phase steel. Iron and Steel, 2017, 52(6): 94-100.

链接本文:

http://www.chinamet.cn/Jweb_gt/CN/10.13228/j.boyuan.issn0449-749x.20160419 或 http://www.chinamet.cn/Jweb_gt/CN/Y2017/V52/I6/94

[1]	徐刚.780MPa级冷轧双相钢的组织与性能.钢铁研究学报。2012，24卷 8期：44-47.
[1]	徐刚.780MPa级冷轧双相钢的组织与性能.钢铁研究学报。2012，24卷 8期：44-47.
[2]	牛枫，赵爱民，赵征志等.铬对超高强冷轧双相钢相变和组织性能的影响.钢铁研究学报.2010,7期：47-50.
[2]	牛枫，赵爱民，赵征志等.铬对超高强冷轧双相钢相变和组织性能的影响.钢铁研究学报.2010,7期：47-50.
[3]	Marcio Milititsky, Paul J Belanger, Matthew S Walp. Advanced steel products for lightweighting at Daimler Chrysler north America[C]// Galvatech 04 ConferencProceedings,2004:52-61.
[3]	Marcio Milititsky, Paul J Belanger, Matthew S Walp. Advanced steel products for lightweighting at Daimler Chrysler north America[C]// Galvatech 04 ConferencProceedings,2004:52-61.
[4]	Engl; B. and Drewes, E.J. New high strength steels with good formability for automotive applications, La Rev. de Mét.-ATS-JSI ,2000:72-77.
[4]	Engl; B. and Drewes, E.J. New high strength steels with good formability for automotive applications, La Rev. de Mét.-ATS-JSI ,2000:72-77.
[5]	P.-O. Norberg.Challenges in the control of reheating and annealing process, Scandinavian Journal of Metallurgy, vol. 26, 1997: 206–214.
[5]	P.-O. Norberg.Challenges in the control of reheating and annealing process, Scandinavian Journal of Metallurgy, vol. 26, 1997: 206–214.
[6]	Atkinson, A. Transport processes during the growth of oxide films at elevated temperature, Rev. Mod. Phys.7 .1985:437-440.
[6]	Atkinson, A. Transport processes during the growth of oxide films at elevated temperature, Rev. Mod. Phys.7 .1985:437-440.
[7]	Douglass, D. L.A critique of internal oxidation in alloys during the post-Wagner era, Oxidation of metals, Vol. 44, 1995: 81-86.
[7]	Douglass, D. L.A critique of internal oxidation in alloys during the post-Wagner era, Oxidation of metals, Vol. 44, 1995: 81-86.
[8]	Baxter, G. P. and Lansing, J. E. The aqueous pressure of some hydrated crystals. Oxalic acid, strontium chloride and sodium sulphate, J. Amer. Chem.Soc. 42 .1920: 419-425.
[8]	Baxter, G. P. and Lansing, J. E. The aqueous pressure of some hydrated crystals. Oxalic acid, strontium chloride and sodium sulphate, J. Amer. Chem.Soc. 42 .1920: 419-425.
[9]	李远鹏，张启富，江社明.双相钢中Si含量对表面氧化物及抑制层形貌的影响.材料热处理学报.2014，35卷1期：151-156.
[9]	李远鹏，张启富，江社明.双相钢中Si含量对表面氧化物及抑制层形貌的影响.材料热处理学报.2014，35卷1期：151-156.
[10]	Pradhan R, Ludkovsky G. Steel sheet continuous Annealing-the HOWAQ Way. Hot and Cold Rolled sheet steels, Warrendale, Pennsylvania, USA:The Metallurgical Society, 1988:57.
[10]	Pradhan R, Ludkovsky G. Steel sheet continuous Annealing-the HOWAQ Way. Hot and Cold Rolled sheet steels, Warrendale, Pennsylvania, USA:The Metallurgical Society, 1988:57.