Development of low temperature pressure vessel steel by Zr-Ti combined deoxidization technology
WANG Bo1，LI Zhu-tie2，Isayev Oleg3，WU Kai-ming3，ZHAN Dong-ping4
（1. College of Engineering， Yantai Nanshan University， Longkou 265713， Shandong， China 2. Technical Center， Shandong Nanshan Aluminum Co.， Ltd.， Longkou 265701， Shandong， China 3. International Research Institute for Steel Technology， Wuhan University of Science and Technology， Wuhan 430081，Hubei， China 4. School of Metallurgy， Northeastern University， Shenyang 110004， Liaoning， China）
Abstract：In order to investigate the effect of Zr-Ti oxides on the mechanical properties of steel， the low temperature pressure vessel steel was manufactured by Zr-Ti combined deoxidization technology replacing Al deoxidization in the process of LD-LF/RH-CC-TMCP-QT. Metallographic microscope， SEM， EDS and mechanical property tests were carried out. The results showed that the fine Zr-Ti compound oxide-sulfide inclusions were formed. The microstructure consisted of predominantly bainite and lots of acicular ferrite， which was homogeneous and fine，with the grain size being more than grade 9. The investigated steel had superior mechanical properties especially the low temperature impact toughness. Its mechanical properties were almost isotropic in transverse and longitudinal directions. The impact absorbed energy reached above 100 J at the temperature of -60 ℃and the DBTT （ductile brittle transition temperature） was lower than -55 ℃. Thus the Zr-Ti combined deoxidization technology had the effect of grain refinement and microstructure homogenization on the steel.
收稿日期: 2017-07-20
出版日期: 2018-02-26
引用本文:
王 博，李铸铁，伊萨耶夫·欧列格，吴开明，战东平. 利用Zr-Ti复合脱氧技术生产低温压力容器钢[J]. , 2018, 53(2): 67-72.
WANG Bo，LI Zhu-tie，Isayev Oleg，WU Kai-ming，ZHAN Dong-ping. Development of low temperature pressure vessel steel by Zr-Ti combined deoxidization technology. Iron and Steel, 2018, 53(2): 67-72.