Abstract:In order to study the decarburization effect of Fe-C alloy strips in Ar-CO-CO2 atmosphere, the decarburization atmosphere was determined by a combination of thermodynamic analysis and experiments. The Fe-C alloy strips were decarburized in mixed 66.25%Ar-25%CO-8.75CO2 gas. Taking the Fe-C alloy strip with an initial carbon content of 4.2% as the research object, the effects of different decarburization temperature, strip thickness and decarburization time on the decarburization effect were studied. The results show that for 2mm thFe-C alloy strips which were decarburized for 60 minutes at 1293K, 1353K, and 1413K, the average carbon content were 2.748%, 1.870%, and 1.134%, respectively. The Fe-C alloy strips with thicknesses of 1mm, 1.5mm and 2mm were decarburizated at 1413K for 60min,the average carbon contents were 0.32%, 0.92% and 1.05% respectively. It has been proved that increasing the decarburization temperature, prolonging the decarburization time and reducing the thickness of the strip all help to improve the decarburization effect .
[1]闫伯骏,邢奕,路培,等.钢铁行业烧结烟气多污染物协同净化技术研究进展[J].工程科学学报, 2018, 40(7):767-[2]洪陆阔,艾立群,程荣,等.铁碳合金薄带气固反应脱碳工艺[J].钢铁研究学报, 2016, 28(5):36-[3]洪陆阔,艾立群,程荣,等.铁碳合金薄带气固反应脱碳试验[J].钢铁, 2016, 51(3):27-[4] Hong L K, Cheng R, Ai L Q, et al.Mechanism of carbon diffusion in the iron Sheet during gas-solid decarburization[J]. [J].Transactions of the India Institute of Metals. , 2019, 72(2):335-[5] Park J O, Long T V, Sasaki Y.Feasibility of solid-state steelmaking from cast iron-decarburization of rapidly solidified cast iron[J]. [J].ISIJ International., 2012, 52(1):26-[6] Lee W H, Park J O, Lee J S, et al.Solid state steelmaking by decarburization of rapidly solidified high carbon iron sheet[J]. [J].Ironmaking and Steelmaking., 2012, 39(7):530-[7] McDonald C.Solid state steelmaking:process technical and economic viability[J]. [J].Ironmaking and Steelmaking., 2012, 39(7):487-[8]程荣,艾立群,洪陆阔,李强等.铁碳合金薄带固态脱碳试验[J].钢铁, 2016, 51(07):28-[9]张凯,陈银莉,孙彦辉,等.加热过程中对弹簧钢脱碳的影响[J].金属学报, 2018, 54(10):1350-[10] Jing Y A, Yuan Y M, Yan X L, et al.Decarburization mechanism during hydrogen reduction descaling of hot-rolled strip steel[J]. [J].International Journal of Hydrogen Energy. , 2017, , 42(15):10611-[11] Ebrahim S S, Mostafa M, Jalil A K, et al.A new approach in solid state steelmaking from thin cast iron sheets through decarburization in CaCO3 pack[J].[J].ISIJ International., 2018, 58(10):1791-[12] Guo L N, Chen J, Zhang M, et al.Decarburization thermodynamics of high-carbon ferromanganese powders during gas-solid fluidization process[J]. [J].Journal of Iron and Steel Research International., 2012, 19(5):1-[13] Guo L N, Chen J, Shi W L, et al.Solid-Phase decarburization of high-carbon ferromanganese powders by microwave heating[J]. [J].Journal of Iron and Steel Research International., 2013, 20(8):34-[14] Luo H W, Xiang R, Chen L F, et al.Modeling the decarburization kinetics in grain-oriented silicon Steels[J]. [J].Chinese Science Bulletin., 2014, 59(15):866-[15] Zheng W S, Lu X G, He Y L, L, et al.Thermodynamic modeling of Fe-C-Mn-Si alloy[J]. [J].Journal of Iron and Steel Research International. , 2017, 24(2):190-[16]Lin J, Luo X N, Zhong X Y, et al.Dislocation pipe diffusion of Mn during annealing of 5Mn steel[J]. [J].Journal of Iron and Steel Research Internationalt. ., 2016, 23(12):1277-