1. Institute of Special Steels, Central Iron and Steel Research Institute, Beijing 100081, China; 2. Collaborative Innovation Center of Steel Generic Technolgy, University of Science and Technology Beijing, Beijing 100083, China
Abstract：In order to study influence of Cu element on the heat resistance property of AMS6308 steel,microstructure and mechanical properties of AMS6308 steel which contains 2%Cu element and steel without Cu as the contrastive test steel at different tempering temperature was studied by SEM,TEM,EBSD,phase analysis and mechanical properties test. And the effect of Cu on increasing temper-resistant of AMS6308 steel was discussed. The results show that strength rises first and then declines with increasing tempering temperature. Maximum peak of strength appears at 450 ℃ tempering temperature. At the whole tempering temperature range,AMS6308 steel has higher strength than steel without Cu. When tempering temperature below 400 ℃,the element Cu promotes strength and temper-resistant depending on the effect of solution strengthening of Cu,enhancing precipitation strengthening of M6C phase and refined crystalline strengthening. And enhancing precipitation strengthening of M6C phase is the main strength method. When tempering temperature exceed 400 ℃,the element Cu promotes strength and temper-resistant depending on the effect of precipitation strengthening of ε-Cu phase. The interaction effect of ε-Cu phase and dislocation produces strong precipitation strengthening and makes the steel maintaining relatively completed lath structure at higher tempering temperature.
赵吉庆, 杨钢, 彭涛. Cu元素对AMS6308钢抗回火性能的影响[J]. 钢铁, 2021, 56(4): 76-82.
ZHAO Ji-qing, YANG Gang, PENG Tao. Effect of Cu on temper-resistant of AMS6308 steel[J]. Iron and Steel, 2021, 56(4): 76-82.
[1] Wright J A,Sebastian J T,Kern C P. Design development and application of new,high-performance gear steels[J]. Gear Technology,2010(1/2):46. [2] Burd E W. A carburizing gear steel for elevated temperatures[J]. Metal Progress,1985(5):33. [3] 赵振业. 航空高性能齿轮钢的研究与发展[J]. 航空材料学报,2000,20(3):148.(ZHAO Zhen-ye. Development of higher-performance aeronautical gear steel[J]. Journal of Aeronautical Materials,2000,20(3):148.) [4] 汤万昌. 我国航空发动机齿轮材料的现状[J]. 航空材料学报,2003,23(s1):283.(TANG Wan-chang. Current status of materials of aero-engine gear in China[J]. Journal of Aeronautical Materials,2003,23(s1):283.) [5] 关云,陈庆丰,李平和. ULCB钢中铜析出行为及对回火性能的影响[J]. 物理测试,2005,23(2):19.(GUAN Yun,CHEN Qing-feng,LI Ping-he. Precipitation of Cu in ULCB steel and its effects on tempering properties[J]. Physics Examination and Testing,2005,23(2):19.) [6] 李振团,柴锋,杨才福,等. 淬火工艺对铜沉淀强化UHS钢组织性能的影响[J]. 钢铁,2019,54(6):79. (LI Zhen-tuan,CHAI Feng,YANG Cai-fu,et al. Effect of quenching process on microstructure and mechanical properties of Cu precipitated hardened ultra-high strength steel[J]. Iron and Steel,2019,54(6):79.) [7] 刘宝锋,杨钢,华建社,等. 淬火温度对AMS 6308钢组织和性能的影响[J]. 特钢技术,2012,18(3):12.(LIU Bao-feng,YANG Gang,HUA Jian-she,et al. effect of quenching temperature on structure and mechanical properties of AMS 6308 steel[J]. Special Steel Techonlogy,2012,18(3):12.) [8] 刘宝锋,杨钢,华建社,等. 成分波动对AMS 6308钢力学性能的影响[J]. 金属热处理,2013,38(4):23.(LIU Bao-feng,YANG Gang,HUA Jian-she,et al. Effect of chemical composition fluctuation on mechanical properties of steel AMS 6308[J]. Heat Treatment of Metals,2013,38(4):23.) [9] 彭涛,曹建春,赵吉庆,等. AMS 6308钢中Cu的析出强化[J]. 材料热处理学报,2016,37(10):126.(PENG Tao,CAO Jian-chun,ZHAO Ji-qing,et al. Cu precipitation strengthening in AMS 6308 steel[J]. Transactions of Materials and Heat Treatment,2016,37(10):126.) [10] 彭涛,赵吉庆,曹建春,等. 退火工艺对AMS 6308钢硬度及组织的影响[J]. 钢铁研究学报,2016,28(4):58.(PENG Tao,ZHAO Ji-qing,CAO Jian-chun,et al. Influence of annealing process on hardness and microstructure of AMS 6308 steel[J]. Journal of Iron and Steel Research,2016,28(4):58.) [11] 彭涛,曹建春,杨钢,等. 预备热处理对AMS6308钢组织及性能的影响[J]. 钢铁,2016,51(8):64.(PENG Tao,CAO Jian-chun,YANG Gang,et al. Effect of preheat treatment on microstructure and mechanical properties of AMS 6308 steel[J]. Iron and Steel,2016,51(8):64.) [12] 董瀚,马党参,郎宇平,等. 钼在合金钢中的特性与应用[J]. 世界有色金属,2010(11):66.(DONG Han,MA Dang-shen,LANG Yu-ping,et al. The characteristics and application of Molybdenum in alloy steel[J]. World Nonferrous Metals,2010(11):66.) [13] 哈森 P. 材料的相变[M]. 北京:科学出版社,2004.(Peter Haasen. Phase Transformations in Materials[M]. Beijing:Science Press,2004.) [14] 雍岐龙. 钢铁材料中的第二相[M]. 北京:冶金工业出版社,2006.(YONG Qi-long. Secondary Phases in Steel[M]. Beijing:Metallurgical Industry Press,2006.)
2021, Vol. 56 