Abstract：Focusing on the development of continuous,efficient and low-cost technology for the synthesis of vanadium carbonitride by one-step method,on the basis of summarizing the research on the production process of vanadium nitride,this paper takes vanadium pentoxide as the raw material,coke as reducing agent,after crushing,mixing and pressing into blocks,drying to reduce the nitride process. The optimum technological conditions for the preparation of vanadium carbonitride by one step carbothermal reduction at high temperature were investigated under high purity nitrogen atmosphere. The reduction process of vanadium pentoxide was thermodynamically analyzed and calculated,and the theoretical analysis was carried out by FactSage thermodynamic software. The single factor test analysis of reaction temperature,reaction time,nitrogen flow rate,pressure and other influencing factors was analyzed by XRD and SEM test methods. The results show that the nitriding reaction of vanadium carbide was carried out step by step,and the reaction process of vanadium carbonitride was V2O5→V2O4→V2O3→VC→VCN. The CO produced in the experiment will change the gas partial pressure in the furnace,which will affect the carbonization temperature and nitriding temperature. Therefore,the CO and N2 partial pressure of the system should be strictly controlled in the reaction process. The reaction time and nitrogen flow rate had different effects on the contents of vanadium,nitrogen and carbon in the reaction products. The vanadium content and nitrogen content increased with the increase of reaction time and nitrogen flow rate,while the carbon content decreased with the increase of reaction time.The pressure determines the porosity of the reactants. On the basis of ensuring the quality of the block product,increasing the sample preparation pressure can increase the contact area between the particles and the specific surface area of the reaction,and the reduction effect is good. Considering comprehensively,setting the carbon distribution coefficient of 35%,sample preparation pressure of 20 MPa,carbothermal reduction at 900 ℃ and nitridation reaction at 1 480 ℃ for 180 min,the test can obtain (mass percent) 75.55%V,13.91%N,4.96%C of vanadium carbonitride products finally,in line with national standards.
杨双平, 张甜甜, 高文彬, 刘守满, 孙海兴. 一步法制备碳氮化钒的工艺优化试验[J]. 钢铁, 2023, 58(1): 170-178.
YANG Shuang-ping, ZHANG Tian-tian, GAO Wen-bin, LIU Shou-man, SUN Hai-xing. Experiment on process optimization of one-step preparation of vanadium carbonitride[J]. Iron and Steel, 2023, 58(1): 170-178.
[1] 柴锋,杨才福,苏航,等. 钒氮微合金化高强度球扁钢的强韧化机制[J]. 钢铁研究学报,2012,24(2):39.(CHAI Feng,YANG Cai-fu,SU Hang,et al. Strengthening and toughening mechanism of hingh strength V-N micro-alloyed bulb-flat steel[J]. Journal of Iron and Steel Research,2012,24(2):39.) [2] 万志健,刘学华,赵海,等. 钒对高碳珠光体钢组织及拉伸性能的影响[J]. 金属热处理,2021,46(3):140.(WAN Zhi-jian,LIU Xue-hua,ZHAO Hai,et al. Effect of V on microstructure and tensile properties of high carbon pearlite steel[J]. Heat Treatment of Metals,2021,46(3):140.) [3] WANG Bo,LI Zhu-tie,ZHAN Dong-ping,et al. Precipitation behavior of VN in high nitrogen and vanadium micro-alloyed low carbon weathering steel[J]. Transactions of the Indian Institute of Metals,2018,71(7):1607. [4] 胡筱旋,王瑞珍,周芸,等. 钒,氮含量对耐磨钢NM400组织及性能的影响[J]. 钢铁,2014,49(10):89.(HU Xiao-xuan,WANG Rui-zhen,ZHOU Yun,et al. Influence of vanadium and nitrogen content on microstructure and properties of NM400 wear-resistant steel[J]. Iron and Steel,2014,49(10):89.) [5] 方芳,雍岐龙,杨才福,等. 碳氮化钒在奥氏体中析出的动力学模型[J]. 钢铁,2008,43(12):71.(FANG Fang,YONG Qi-long,YANG Cai-fu,et al. A model for the kinetics of V(C,N)precipitation in austenite[J]. Iron and Steel,2008,43(12):71.) [6] CHEN Lu-yang,GU Yun-le,SHI Liang,et al. A room-temperature synthesis of nanocrystalline vanadium nitride[J]. Solid State Communications,2004,132(5):343. [7] 马江南,杨才福,王瑞珍. 增氮对钒微合金钢组织和性能的影响[J]. 钢铁,2015,50(4):63.(MA Jiang-nan,YANG Cai-fu,WANG Rui-zhen. Influence of nitrogen addition on the microstructure and properties of vanadium microalloyed steel[J]. Iron and Steel,2015,50(4):63.) [8] 于三三,付念新,高峰,等. 一步法合成碳氮化钒的动力学研究[J]. 稀有金属,2008(1):84.(YU San-san,FU Nian-xin,GAO Feng,et al. Chemical kinetics of synthesizing vanadium carbonitride by one step method[J]. Chinese Journal of Rare Metals,2008(1):84.) [9] 杨勇,吴伟,刘浏. 五氧化二钒制备碳氮化钒的试验研究[J]. 钢铁钒钛,2018,39(2):25.(YANG Yong,WU Wei,LIU Liu. Experimental study on preparation of vanadium carbonitride by vanadium pentoxide[J]. Iron Steel Vanadium Titanium,2018,39(2):25.) [10] 王勇围,桂美文,沈金龙,等. 热变形对钒、氮微合金化钢77B性能的影响[J]. 钢铁研究学报,2010,22(10):30.(WANG Yong-wei,GUI Mei-wen,SHEN Jin-long,et al. Effection of thermal deformation on properties of V,N micro-alloyed steel 77B[J]. Journal of Iron and Steel Research,2010,22(10):30.) [11] 杨才福. 钒微合金化钢的技术进展与应用[J]. 钢铁研究学报,2020,32(12):1029.(YANG Cai-fu. Recent development and applications of vanadium microalloying technology[J]. Journal of Iron and Steel Research,2020,32(12):1029.) [12] Zaki Z I,El-Sadek M H,Ali H H,et al. Synthesis of vanadium carbide by mechanical activation assisted carbothermic reduction[J].Materials,2020,13(19):4408. [13] 卿家胜,沈厚发,刘明. 高强耐候钢YQ450 NQR1钒氮微合金化[J]. 钢铁,2017,52(5):87.(QING Jia-sheng,SHEN Hou-fa,LIU Ming.V-N microalloying of high strength weathering steel YQ450 NQR1[J]. Iron and Steel,2017,52(5):87.) [14] 杨才福. 钒钢的技术进展[J]. 钢铁,2013,48(4):1.(YANG Cai-fu. Recent development of vanadium microalloying technology[J]. Iron and Steel,2013,48(4):1.) [15] 王安仁,陈立平,张庆春. V2O5制备VN的还原氮化机理[J]. 过程工程学报,2013,13(4):704.(WANG An-ren,CHEN Li-ping,ZHANG Qing-chun. Carbothermal reduction and nitridation mechanism of VN prepared by V2O5[J]. The Chinese Journal of Process Engineering,2013,13(4):704.) [16] 彭雄,肖亚,王绍斌,等. 钒氮合金化热轧抗震钢筋HRB400E产品开发[J]. 中国冶金,2019,29(1):25.(PENG Xiong,XIAO Ya,WANG Shao-bin,et al. Development of V-N alloyed hot rolled ribbed bar HRB400E[J]. China Metallurgy,2019,29(1):25.) [17] 吴跃东,张国华,周国治. 碳热还原氮化法制备氮化钒铁合金的研究[J]. 铁合金,2017,48(6):31.(WU Yue-dong,ZHANG Guo-hua,ZHOU Guo-zhi. Study on the preparation of ferrovanadium nitride via carbothermic reduction process[J]. Ferro-Alloys,2017,48(6):31.) [18] 杨勇,张曦东,姚同路,等. 碳热还原渗氮法制备钒氮合金的试验[J]. 钢铁,2018,53(4):67.(YANG Yong,ZHANG Xi-dong,YAO Tong-lu,et al. Experiment on preparation of vanadium nitrogen alloy by carbothermal reduction and nitriding[J]. Iron and Steel,2018,53(4):67.) [19] YU San-san,FU Nian-xin,GAO Feng,et al. Synthesis of vanadium nitride by a one step method[J]. Journal of Materials Science and Technology,2007(1):45. [20] 韩静利,张一敏,刘涛,等. 还原氮化一步法制备氮化钒[J]. 有色金属(冶炼部分),2018(6):51.(HAN Jing-li,ZHANG Yi-min,LIU Tao,et al. Preparation of vanadium nitride by one step method of reduction and nitridation[J]. Nonferrous Metals(Extractive Metallurgy),2018(6):51. [21] 薛正良,陈志超,王炜,等. 碳热还原氮化一步法制备钒氮合金工艺研究[J]. 武汉科技大学学报,2012,35(3):161.(XUE Zheng-liang,CHEN Zhi-chao,WANG Wei,et al. One-step method of carbon thermal reduction and nitridation to produce vanadium nitrogen alloy[J]. Journal of Wuhan University of Science and Technology,2012,35(3):161.) [22] 董江,薛正良,余岳. V2O5还原氮化一步法合成氮化钒[J]. 太原理工大学学报,2014,45(2):168.(DONG Jiang,XUE Zheng-liang,YU Yue. Synthesis of vanadium nitride with reduction and nitridation by one-step method from V2O5[J]. Journal of Taiyuan University of Technology,2014,45(2):168.) [23] 吴铿,折媛,刘起航,等. 高炉大型化后对焦炭性质及在炉内劣化的思考[J]. 钢铁,2017,52(10):1.(WU Keng,SHE Yuan,LIU Qi-hang,et al. Consideration on properties of coke and coke deterioration after large-scale blast furnace[J]. Iron and Steel,2017,52(10):1.) [24] 张建良,孙敏敏,李克江,等. 高炉焦炭在铁水中溶解行为研究现状及展望[J]. 钢铁,2020,55(4):1.(ZHANG Jian-liang,SUN Min-min,LI Ke-jiang,et al. Present situation and prospect of dissolution behavior of metallurgical coke in blast furnace hot metal[J]. Iron and Steel,2020,55(4):1.) [25] 喻雄,孙丽枫,王鹤松,等. 提钒尾渣碳热还原过程实验[J]. 重庆大学学报,2015,38(2):123.(YU Xiong,SUN Li-feng,WANG He-song,et al. Analysis on transfer and enrichment of metal elements during reduction roasting of vanadium tailings[J]. Journal of Chongqing University,2015,38(2):123. [26] 姜中涛,刘颖,陈巧旺,等. V2O5碳热还原合成碳化钒粉末的反应过程[J]. 粉末冶金技术,2012,30(1):40.(JIANG Zhong-tao,LIU Ying,CHEN Qiao-wang,et al. Reaction process of synthesizing vanadium carbide powder by vanadium pentoxide carbothermal reduction[J]. Powder Metallurgy Technology,2012,30(1):40.) [27] 李明波. 钒氮合金成型工艺优化[J]. 山东冶金,2021,43(5):33.(LI Ming-bo. Optimization of forming process of vanadium-nitrogen alloy[J]. Shandong Metallurgy,2021,43(5):33.) [28] 孙静,彭程,石志霞,等. 碳热还原法制备V2O3的研究[J]. 金属功能材料,2016,23(3):47.(SUN Jing,PENG Cheng,SHI Zhi-xia,et al. Preparation of V2O3 by carbon thermal reduction[J]. Metallic Functional Materials,2016,23(3):47.) [29] 方民宪,陈厚生. 碳热还原法制取VC、VN和V(C,N)的热力学原理研究[J]. 矿冶,2007(3):46.(FANG Min-xian,CHEN Hou-sheng. Study on thermodynamic principle of preparztion of VC、VN and V(C,N) by carbon-heat reducing[J]. Mining and Metallurgy,2007(3):46.) [30] 田键,周昱,黄红旗,等. 氮化钒形成机制中热动力学及活化能研究[J]. 兵器材料科学与工程,2016,39(5):1.(TIAN Jian,ZHOU Yu,HUANG Hong-qi,et al. Thermokinetics and activation energy in formation mechanism of vanadium nitride[J]. Ordnance Material Science and Engineering,2016,39(5):1.) [31] 徐先锋,王玺堂. 五氧化二钒制备氮化钒的过程研究[J]. 钢铁钒钛,2003(1):46.(XU Xian-feng,WANG Xi-tang. Research on reduction and nitrogenization process for preparing VN from V2O5[J]. Iron Steel Vanadium Titanium,2003(1):46.) [32] 邓莉,刘颖,姜中涛,等. 碳热还原氮化法制备碳氮化钒的研究[J]. 功能材料,2010,41(5):840.(DENG Li,LIU Ying,JIANG Zhong-tao,et al. Synthesis of vanadium carbonitride by carbothermal reduction and nitridation method[J]. Journal of Functional Materials,2010,41(5):840.)
2023, Vol. 58 