Model of “Liquid Window” by Calcium Treatment in Medium Carbon Steel |
MA Zhi-fei1,SUN Yan-hui1,ZENG Ya-nan1,AI Xi1,LIU Rui-ning2,LIU Yong2 |
1. School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing,Beijing 100083, China 2. Shijiazhuang Iron and Steel Group Corporation,Shijiazhuang 050000, Hebei, China |
|
|
Abstract The variations of inclusion types in Q345B steel was investigated before and after calcium treatment. The modification mechanism of alumina and the condition of the precipitation of calcium sulfide were analyzed by thermodynamics. Meanwhile, the model of “liquid window” regarding the modification of inclusions was established. Thermodynamic calculations show that : in order to modify the alumina inclusions to liquid calcium aluminate, the content of calcium in steel from 0.0017% to 0.0102% is needed when the aluminum in steel is 0.016% at 1873K. The result of industrial production reveals that alumina can be modified into 12CaO·7Al2O3 or CaO·Al2O3 inclusion when the content of calcium in steel is between 0.0014%and 0.0017%. While MnS just can be partially modified into CaS and no single precipitation of CaS occurred.
|
Received: 15 March 2013
Published: 25 November 2013
|
|
|
|
|
[1] |
QIN Zheng-feng, XUE Zheng-liang, LI Jin-bo, LI Bo-si. Origin of large spherical or bar-shaped inclusions in calcium treated steel[J]. Iron and Steel, 2020, 55(5): 31-38. |
[2] |
YANG Guang-wei, CHEN Zhao-ping, LIU Xiang-chun. Effect of non-calcium treatment on inclusions in high grade case hardening steel[J]. Iron and Steel, 2020, 55(4): 40-44. |
[3] |
. Analysis and Research on nodulation phenomenon of aluminum deoxidized sulfur-containing steel[J]. , 2020, 45(3): 0-0. |
[4] |
LIU Zhen-tong, YANG Wen, REN Ying, ZHANG Li-feng, WANG Wei-jian. Analysis of influencing factors on effect of calcium treatment in Al-killed steels[J]. Iron and Steel, 2020, 55(3): 29-34. |
[5] |
ZHU Cheng-yi1,2,HUANG Luo-yi1,2,LUO Xiao-yan1,2,LIU Yu-long1,2,WANG Yong1,2,LI Guang-qiang1,3. Effect of calcium treatment on characteristics of inclusions in finished non-oriented silicon steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(2): 117-128. |
[6] |
XIAO Zunhu1,LIU Peng2,XU Gangjun2,ZHOU Junjun2,SUI Yafei2. Selection of calcium treatment technology of LF #br#
refining for different steel[J]. Iron and Steel, 2019, 54(9): 62-72. |
|
|
|
|