| Change in Composition of Mold Flux and Its Effects on Properties During Casting 304HC Stainless Steel |
| WANG Xinyue,JIN Shantong |
| School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China |
|
|
|
|
Abstract The change in mold flux composition, caused by the products (products of deoxidation and products of reoxidation as the results of chemical reactions on inner slagmetal interface, and inclusions from refractories) which were finally absorbed by mold flux, and its effects on flux properties were investigated by sampling mold flux during continuous casting of 304HC and analysis. By comparing these samples with the original flux, it was found that Al2O3 and Cr2O3 contents of mold flux were increased, F content was decreased and basicity of mold flux was reduced during casting. And all of these caused the change in properties of molten flux, such as viscosity, solidification temperature and the crystalline fraction of slag film. The results are good for the rational design of mold flux during casting of stainless steel and reducing the surface defects of stainless steel cast piece.
|
|
Received: 01 January 1900
|
|
|
|
| [1] |
WEI Tong-yu, ZOU De-ning, ZHANG Ying-bo, CHEN Wan-wan. Effect of aluminum on microstructure and properties of high alumina ferritic heat resistant steel[J]. Iron and Steel, 2020, 55(6): 80-83. |
| [2] |
LI Ji-wu, CAO Qian-qian, YANG Hai-ru. Thinning of 304 stainless steel pipeline under impact fretting wear[J]. Iron and Steel, 2020, 55(6): 118-122. |
| [3] |
LIU Ke, HAN Yi-hua, YANG Fan, ZHU Li-guang. Effect of MgO on microstructure of CaO-Al2O3 based quaternary system mold fluxes[J]. Iron and Steel, 2020, 55(5): 52-58. |
| [4] |
ZHAO Yun-peng, YU Chao, XIAO Hong, WU Zong-he, XU Peng-peng, XIE Hong-biao. Effect of pure iron interlayer on mechanical properties of hot rolled stainless steel clad plate[J]. Iron and Steel, 2020, 55(5): 73-79. |
| [5] |
WU Xiang-yu, HE Yu-dong, WU Liang-ping, SHEN Ping, FU Jian-xun. Effect of magnesium modification on sulfides in Y1Cr13 free-cutting stainless steel[J]. Iron and Steel, 2020, 55(4): 68-74. |
| [6] |
zheng yuanshou. High speed production technology of 160 × 160mm2 continuous casting in SanGangsteel[J]. , 2020, 45(3): 0-0. |
|
|
|
|
2006, Vol. 41 