| Investigation on Head Slab Cleanliness of Low Carbon Aluminum Killed Steel |
| YANG Wen1,XUE Yong-qiang2，CAO Jing1,WANG Xin-hua1,WANG Wan-jun1 |
1. School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China
2. Manufacturing Department，Shougang Jingtang United Iron and Steel Co., Ltd., Tangshan 063200, Hebei, China |
|
|
|
|
Abstract High cleanliness is required for low carbon aluminum killed (LCAK for short) steel which is widely used for production of cold rolled sheet. But, head slab cleanliness is seriously deteriorated by the unsteady casting condition at casting start stage. Cleanliness of LCAK steel head slab was systemically investigated on aspects of slab composition and non-metallic inclusions under the present casting conditions. Besides, factors affecting the cleanliness of head slab were discussed. A cast starting number is defined.The results show that the head slab cleanliness is unstable until the number reaches 0.17, which can help slab quality classification. The main factor deteriorating head slab is the reoxidation in tundish. Besides oxygen in the air, more extent of reoxidation is caused by the refractory and covering slag in tundish. Several measures of improving head slab cleanliness were put forward as well, which can provide certain reference on plant operations.
|
|
Received: 25 October 2010
Published: 09 October 2011
|
|
|
|
| [1] |
YAN Xue-qiang1,2,ZHENG Wan1,2,WANG Guo-wei1,2,YAN Wen1,LI Guang-qiang1,2. Effect of microporous MgO refractories on steel cleanliness[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(6): 483-490. |
| [2] |
LI Xiao-yuan,SHI Jie. Ballistic behavior of high strength steel targets during high speed impact of projectile[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(5): 429-436. |
| [3] |
LIU Peng, SUI Ya-fei, XU Gang-jun, ZHOU Jun-jun, ZENG Quan-wen. Inclusion generation and control of low carbon steel[J]. Iron and Steel, 2020, 55(2): 67-74. |
| [4] |
HUANG Caide,HE Wenyuan,LIU Yanqiang,XIAO Maoyuan,. Effect of electromagnetic braking on flow field in #br#
tinplate under high casting speed[J]. Iron and Steel, 2019, 54(8): 90-101. |
| [5] |
XU Jian-fei，，LIU Zhi-yuan，WANG Chong-jun，CHENG Ju-guang， TIAN Bao-yi，ZHANG Jie. Study on inclusion control during the slab continuous casting process.[J]. , 2018, 43(6): 61-66. |
| [6] |
TANG De-chi ，ZHANG Hong-yan ，JI Li-peng， XIAO Bao-liang ，ZHANG Da-wei ，ZENG Zhi . Cleanliness of calcium-treated wheel steel[J]. Iron and Steel, 2018, 53(4): 37-41. |
|
|
|
|
2011, Vol. 46 