Mixed Crystal of Inherent Grain Size in Track Pins 1E1158M Steel |
1, 1, 1, 1 |
|
|
Abstract 1E1158M steel developed by Caterpillar is used for track pin and the final heat treatment is quenching and tempering. However, the inherent grain size appears mixed crystal after final heat treatment, which affects the performance. In this paper, the thermal simulation test and the quantitative analysis of microstructure were carried out to investigate the mixed crystal phenomenon of inherent grain size of 1E1158M steel under different finishing temperatures. The results show that the abnormal grain growth temperature of hot-rolled and normal-fired microstructures is both 850°C, and the finishing rolling temperature has an effect on mixed crystal degree. When the finish rolling temperature is 850°C, the austenite grains are partially recrystallized at the end of rolling, and the degree of mixed crystals is serious. As the finishing temperature increases, the inhomogeneity of the intrinsic grain size decreases and the recommended finishing temperature is 1000°C.
|
Received: 26 February 2020
Published: 16 October 2020
|
|
|
|
|
[1]邓安华.金属材料简明辞典[M]. 北京: 冶金工业出版社, 1992.
[2]关小军, 凤佩华.终轧温度对-板组织和性能的影响[J].工程科学学报, 1995, 17(3):249-253
[3]Yang H L, Xu G, Wang L, et al..A study of growth of austenite grains in a steel microalloyed with Ti and Nb[J]. Metal science and heat treatment., 2017, 59(1-2):8-13
[4]in Chi-kang, Su Yen-hao, Hwang Weng-sing, et al.On pinning effect of austenite grain growth in Mg-containing low-carbon steel[J].Materials Science and Technology, 2018, 34(5):596-606
[5]莫伟灵.热加工工艺对奥氏体本质晶粒度的影响 [J].特殊钢, 1980, ( (2)):96-104
[6]吴志方, 况嘉伦, 石俊, 等.工艺生产热轧钢板显微组织混晶的产生和消除[J].热加工工艺, 2013, 42(11):105-107
[7]董芳.锻造及预备热处理工艺对18Cr2Ni4WA锻件本质晶粒度的影响[J].金属加工(热加工), 2017, ( (11)): 61-64
[8]鸣图, 黄承江, 王中丙, 等.高成型性细晶粒级热轧汽车板的开发和应用研究[J].材料导报, 2004, 18(8):110-113
[9]尚呈, 周立新, 张志成, 等.热处理工艺对钢奥氏体晶粒度的影响[J].金属热处理, 2014, 39(11):111-113
[10]蔡仲卫.履带销轴用1E1158M钢的生产实践[J][J].河北冶金,, 2012, ( (6)):39-40
[11]毛卫民, 赵新兵. 金属的再结晶与晶粒长大[M]. 北京: 冶金工业出版社, 1994. .
[12]常铁军, 马茂元.钢的混晶程度评价方法探讨[J].理化检验物理分册, 1989, ((1)):41-41
[13]Pous-Romero H, Lonardelli I, Cogswell D, et al.Austenite grain growth in a nuclear pressure vessel steel[J][J].Materials science and engineering, 2013, ((567)):72-79
[14]徐厚训, 栗牧怀.对结构钢(40CrNiMoA)奥氏体本质晶粒度影响因素的探讨[J].材料工程, 1983, ( (2)):16-20
[15]赵勇桃, 刘宗昌, 王玉峰.钢的混晶及消除措施[J].金属热处理, 2007, 32(5):75-77
|
[1] |
LIU Zhi-wei, LI Yang, LI Zhong-hua, [LU]Yao-qiang, GAO Yan, BAI Min. Analysis of roll cracking of high-strength automobile beam steel[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(5): 27-. |
[2] |
WANG Huan, HU Jia-li, ZHANG Chao-lei, LI Jian, MIAO Hong-sheng. Mixed crystal of austenite grain size in track pins 1E1158M steel[J]. Iron and Steel, 2020, 55(11): 126-132. |
[3] |
. Study on the transformation behavior and microstructure during hot-charging rolling process in a 12Cr1MoV heat-resistance steel[J]. , 2019, 44(4): 0-0. |
[4] |
YANG Jun,GAO Jian-hong,YANG Qi-yu. Effect of hot-rolling technology on surface chromatic aberration defects for Ti precipitation strengthened steel[J]. Iron and Steel, 2018, 53(2): 45-49. |
[5] |
LI Wen-yuan, LIU Kun, HUI Ya-jun, LIU Xiao-cui, LIU Jie, LI Zheng-quan. Effect of .nish rolling temperature on microstructure and mechanical properties of hot rolled high strength steel for container[J]. Chinese Journal of Iron and Steel, 2015, 27(8): 64-69. |
[6] |
CONG Jie,WU Peng. Failure analysis of 54SiCr6 spring[J]. Chinese Journal of Iron and Steel, 2015, 33(5): 48-50. |
|
|
|
|