齿轮钢矩形坯皮下裂纹的成因

郭秋实,文光华,程维玮,王端军,孔凡杰

钢铁研究学报 ›› 2012, Vol. 24 ›› Issue (03) : 28-31.

钢铁研究学报 ›› 2012, Vol. 24 ›› Issue (03) : 28-31.
材料研究

齿轮钢矩形坯皮下裂纹的成因

  • 郭秋实1,文光华1,程维玮2,王端军2,孔凡杰2
作者信息 +

Investigation on Subsurface Cracks of Rectangular Bloom for Gear Steel

  • GUO Qiu-shi1,WEN Guang-hua1,CHENG Wei-wei2,WANG Duan-jun2,KONG Fan-jie2
Author information +
文章历史 +

摘要

利用光学显微镜、扫描电镜和能谱仪分析了齿轮钢矩形坯皮下裂纹的特征及成因。结果表明:皮下裂纹产生于矩形坯铸坯侧面,距离表面1~5mm,具有明显位置性;结晶器中钢液凝固前沿聚集的Al2O3夹杂物是皮下裂纹形成的主要原因;改变浸入式水口类型和控制钢水过热度可以改善结晶器中夹杂物分布和促进夹杂物上浮,避免皮下裂纹的产生,同时防止了棒材表面线纹的发生。

Abstract

The character and cause of subsurface cracks on gear steel rectangular bloom were investigated by means of microscope, SEM and EDS. The results show that subsurface cracks which is 1-5mm far from surface, appears the sides of casting and have the obvious position. The main reason of subsurface cracks formation is that there exist mass Al2O3 inclusions in the front of steel liquid solidification in the mould. Changing the distribution of inclusions and promoting floatation of inclusions in the mould by changing into the nozzles types and controlling the degree of superheat can avoid producing subsurface cracks and streak defects in rod surface.

关键词

齿轮钢 / 矩形坯 / 皮下裂纹 / 夹杂物

Key words

gear steel / rectangular bloom / subsurface cracks / inclusions

引用本文

导出引用
郭秋实,文光华,程维玮,王端军,孔凡杰. 齿轮钢矩形坯皮下裂纹的成因[J]. 钢铁研究学报, 2012, 24(03): 28-31
GUO Qiu-shi1,WEN Guang-hua1,CHENG Wei-wei2,WANG Duan-jun2,KONG Fan-jie2. Investigation on Subsurface Cracks of Rectangular Bloom for Gear Steel[J]. Journal of Iron and Steel Research, 2012, 24(03): 28-31
中图分类号: TF777.1   

参考文献

[1] 王志道.低倍检验在连铸生产中的应用和图谱[M].北京:冶金工业出版社,2009,1.
[2] G.Das,Sukomal Ghosh. Investigation of sub-surface cracks in continuous cast billets[J]. Engineering Failure Analysis,2003,10:363-370.
[3] 秦影,刘辉霞等.连铸坯低倍缺陷的产生原因及控制[J].河北冶金,2004,4:41-43.
[4] 韩志强,蔡开科.连铸坯内裂纹形成条件的评述[J].钢铁研究学报,2001,13(1):2.
[5] 袁伟霞.连铸坯凝固过程应变及内裂纹研究[J].炼钢,2001,17(2):48-51.
[6] 蔡开科.浇注与凝固[M].北京:冶金工业出版社,1987.
[7] 陈远清.攀钢四流大方坯连铸中间包和结晶器的数理模拟研究[D].重庆:重庆大学硕士学位论文,2006,4.
[8] 蔡开科.连铸坯质量控制[M].北京:冶金工业出版社,2010.
[9] Samarasekera I V, Brimacombe J K. The Thermal Field in Continuous Casting Mould[J]. Canadian Metallurgical Quarterly, 1979,18:251-266.

48

Accesses

0

Citation

Detail

段落导航
相关文章

/