ժҪ In the present paper, tensile tests of Fe-30Mn-5Si -2Al steel were carried out for different strains of 0.05, 0.14, 0.26, and up to the strain-to-failure in order to observe the evolution of microstructure during deformation and investigate the strain hardening behavior. Three-stage strain hardening behavior was observed in this steel during tensile test. In stage I, planar dislocation structure was observed by TEM to be the main deformation mechanism, and low strain hardening rate exponent was exhibited. Primary deformation twinning occurred in stage II, and the strain hardening rate exponent increased due to the blockage of dislocations�� motion by twin boundaries. In stage III, the strain hardening rate exponent had increased to be higher than 0.5. The obstacle effect of twin boundaries and twin-twin interaction had been observed by TEM, and the interactions between primary and secondary twins were found to cause the additional hardening in addition to the obstacle effect on dislocations�� motion, which led to the twinning induced plasticity effect in the later stage of deformation.
Abstract��In the present paper, tensile tests of Fe-30Mn-5Si -2Al steel were carried out for different strains of 0.05, 0.14, 0.26, and up to the strain-to-failure in order to observe the evolution of microstructure during deformation and investigate the strain hardening behavior. Three-stage strain hardening behavior was observed in this steel during tensile test. In stage I, planar dislocation structure was observed by TEM to be the main deformation mechanism, and low strain hardening rate exponent was exhibited. Primary deformation twinning occurred in stage II, and the strain hardening rate exponent increased due to the blockage of dislocations�� motion by twin boundaries. In stage III, the strain hardening rate exponent had increased to be higher than 0.5. The obstacle effect of twin boundaries and twin-twin interaction had been observed by TEM, and the interactions between primary and secondary twins were found to cause the additional hardening in addition to the obstacle effect on dislocations�� motion, which led to the twinning induced plasticity effect in the later stage of deformation.
WANG Shu��han;LIU Zhen��yu;WANG Guo��dong;et al. Effects of Twin-Dislocation and Twin-Twin Interactions on the Strain Hardening Behavior of TWIP Steels[J]. �й������ڿ���, 2010, 17(12): 70-74.
WANG Shu��han;LIU Zhen��yu;WANG Guo��dong;et al. Effects of Twin-Dislocation and Twin-Twin Interactions on the Strain Hardening Behavior of TWIP Steels. Chinese Journal of Iron and Steel, 2010, 17(12): 70-74.
2010, Vol. 17 