ժҪ Liquid��phase enhanced sintering of powder metallurgy (P/M) 316L stainless steel by addition of sintering aids was studied. 2%-8% of pre��alloyed Fe��Mo��B powder with two different particle sizes was added as sintering aids, and the specimens were sintered in vacuum at 1 200-1 350 ��. The results show that the fine Fe��Mo��B powder (5-10 ��m) has stronger activated effect. The sintered density increases with the increase in sintering aid content or sintering temperature. Warm compaction has a better effect on the control of dimensional precision of compacts. The prealloyed Fe��Mo��B powder deviated from Mo2FeB2 component can also be sintering aid of P/M 316L stainless steel.
Abstract��Liquid��phase enhanced sintering of powder metallurgy (P/M) 316L stainless steel by addition of sintering aids was studied. 2%-8% of pre��alloyed Fe��Mo��B powder with two different particle sizes was added as sintering aids, and the specimens were sintered in vacuum at 1 200-1 350 ��. The results show that the fine Fe��Mo��B powder (5-10 ��m) has stronger activated effect. The sintered density increases with the increase in sintering aid content or sintering temperature. Warm compaction has a better effect on the control of dimensional precision of compacts. The prealloyed Fe��Mo��B powder deviated from Mo2FeB2 component can also be sintering aid of P/M 316L stainless steel.
YANG Xia;GUO Shi��ju. Fe��Mo��B Enhanced Sintering of P/M 316L Stainless Steel[J]. �й������ڿ���, 2008, 15(1): 10-0.
YANG Xia;GUO Shi��ju. Fe��Mo��B Enhanced Sintering of P/M 316L Stainless Steel. Chinese Journal of Iron and Steel, 2008, 15(1): 10-0.