Experimental and Simulation Studies on Fabricating GCr15/40Cr Bimetallic Compound Rollers Using Electroslag Surfacing with Liquid Metal Method
Lei RAO1,Shuang-jun WANG1,Jian-hua ZHAO1,Mao-peng GENG2,Gang DING3
1. College of Mechanical and Electronic Engineering, Hohai University, Changzhou 213022, Jiangsu, China 2. College of Mechanical and Electronic Engineering, Nanchang University, Nanchang 330031, Jiangxi, China 3. Xinya Special Steel Forging Co., Ltd., Danyang 212322, Jiangsu, China
Experimental and Simulation Studies on Fabricating GCr15/40Cr Bimetallic Compound Rollers Using Electroslag Surfacing with Liquid Metal Method
Lei RAO1,Shuang-jun WANG1,Jian-hua ZHAO1,Mao-peng GENG2,Gang DING3
1. College of Mechanical and Electronic Engineering, Hohai University, Changzhou 213022, Jiangsu, China 2. College of Mechanical and Electronic Engineering, Nanchang University, Nanchang 330031, Jiangxi, China 3. Xinya Special Steel Forging Co., Ltd., Danyang 212322, Jiangsu, China
ժҪ Electroslag surfacing with liquid metal (ESSLM) is an excellent method for producing high-quality bimetallic compound rollers. The quality of each compound roller is primarily determined by the metallurgical quality of the combined interface. A GCr15/40Cr compound roller is produced using an ESSLM non-consumable electrode electroslag heating method. The temperature and electric fields produced by the ESSLM system are calculated. As the roller core moves downward in the mold, it passes through five sections: the preheating section, the rapid heating section, the temperature homogenizing section, the bimetal fusing section and the cooling section which listed from the top to bottom of the mold, respectively. The temperature distribution and the degree of the surface temperature fluctuation in the roller core are different for each section. Near the combined interface, four layers are found from the roller core to the cladding layer: the remelting layer, the fusion layer, the interface solidification layer and the chilling layer, respectively. Among these, the fusion and interface solidification layers are the key transition zones that greatly influence the combination quality. The surface temperature of the roller core prior to cladding is mainly determined by the drawing velocity, and the thickness of the transition layer increases as the drawing velocity decreases. A transition layer that is too thick or too thin will reduce the mechanical properties at the combined interface. Therefore, the drawing velocity should be limited to a moderate range to produce a satisfactory bimetallic compound roller.
Abstract��Electroslag surfacing with liquid metal (ESSLM) is an excellent method for producing high-quality bimetallic compound rollers. The quality of each compound roller is primarily determined by the metallurgical quality of the combined interface. A GCr15/40Cr compound roller is produced using an ESSLM non-consumable electrode electroslag heating method. The temperature and electric fields produced by the ESSLM system are calculated. As the roller core moves downward in the mold, it passes through five sections: the preheating section, the rapid heating section, the temperature homogenizing section, the bimetal fusing section and the cooling section which listed from the top to bottom of the mold, respectively. The temperature distribution and the degree of the surface temperature fluctuation in the roller core are different for each section. Near the combined interface, four layers are found from the roller core to the cladding layer: the remelting layer, the fusion layer, the interface solidification layer and the chilling layer, respectively. Among these, the fusion and interface solidification layers are the key transition zones that greatly influence the combination quality. The surface temperature of the roller core prior to cladding is mainly determined by the drawing velocity, and the thickness of the transition layer increases as the drawing velocity decreases. A transition layer that is too thick or too thin will reduce the mechanical properties at the combined interface. Therefore, the drawing velocity should be limited to a moderate range to produce a satisfactory bimetallic compound roller.
��������:National Key Basic Research and Development Program of China
ͨѶ����:
����
E-mail: rao_lei@163.com
����:
Lei RAO,Shuang-jun WANG,Jian-hua ZHAO,Mao-peng GENG,Gang DING. Experimental and Simulation Studies on Fabricating GCr15/40Cr Bimetallic Compound Rollers Using Electroslag Surfacing with Liquid Metal Method[J]. �й������ڿ���, 2014, 21(9): 869-877.
Lei RAO,Shuang-jun WANG,Jian-hua ZHAO,Mao-peng GENG,Gang DING. Experimental and Simulation Studies on Fabricating GCr15/40Cr Bimetallic Compound Rollers Using Electroslag Surfacing with Liquid Metal Method. Chinese Journal of Iron and Steel, 2014, 21(9): 869-877.
2014, Vol. 21 