Influence of Residual Stress on Shape of Heavy-gauge, High-strength Steel Caused by Cooling Process after Hot Rolling
1. School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China 2. Research and Development Center, Wuhan Iron & Steel Group Co., Ltd., Wuhan 430080, Hubei, China
ժҪ The cooling process following hot rolling has a significant effect on the shape quality of a hot-rolled strip. The temperature and stress fields in the cooling process for a 14 mm thick strip with yield strength of 500 MPa grade were analyzed by the finite element method and actual test data, and the relationship between residual stress and shape defects was described. Subsequently, the small-crown rolling process and the coil slow cooling process were investigated. The results indicate that these processes improved the shape quality of the final product significantly.
Abstract��The cooling process following hot rolling has a significant effect on the shape quality of a hot-rolled strip. The temperature and stress fields in the cooling process for a 14 mm thick strip with yield strength of 500 MPa grade were analyzed by the finite element method and actual test data, and the relationship between residual stress and shape defects was described. Subsequently, the small-crown rolling process and the coil slow cooling process were investigated. The results indicate that these processes improved the shape quality of the final product significantly.
��������:National Natural Science Foundation of China
ͨѶ����:
������
E-mail: kangylin@ustb.edu.cn
����:
Shui-ze WANG,,Yong-lin KANG,Guo-ming ZHU,Wen LIANG. Influence of Residual Stress on Shape of Heavy-gauge, High-strength Steel Caused by Cooling Process after Hot Rolling[J]. �й������ڿ���, 2016, 23(6): 547-552.
Shui-ze WANG,,Yong-lin KANG,Guo-ming ZHU,Wen LIANG. Influence of Residual Stress on Shape of Heavy-gauge, High-strength Steel Caused by Cooling Process after Hot Rolling. Chinese Journal of Iron and Steel, 2016, 23(6): 547-552.
2016, Vol. 23 