1. School of Material Science and Engineering, Jiangsu University, Zhenjiang 212013, Jiangsu, China 2. School of Mechanical and Automotive Engineering, South China University of Technology, Guangzhou 510641, Guangdong, China
Effects of TMCP Schedule on Precipitation, Microstructure and Properties of Ti-microalloyed High Strength Steel
1. School of Material Science and Engineering, Jiangsu University, Zhenjiang 212013, Jiangsu, China 2. School of Mechanical and Automotive Engineering, South China University of Technology, Guangzhou 510641, Guangdong, China
ժҪ Using the similar compositions of the Ti-microalloyed high-strength steels produced by the thin-slab casting process of compact strip production (CSP), four thermo-mechanical control processes(TMCP) after the simulated thick-slab casting, i.e. the two hot rolling routes and the two cooling processes, were designed, aiming at achieving the same mechanical properties as the thin strip products. The final microstructures after the four TMCP processes were examined by optical microscope(OM), scanning electron microscope(SEM) and transmission electron microscope (TEM). The tensile properties and Charpy impact energy were measured correspondingly. Strain-induced TiC precipitation was found in the two-stage rolling route with the finish rolling temperature at low levels, leading to grain refinement due to the pinning effect during austenite recrystallization. Precipitation hardening in ferrite was observed when a period of isothermal holding was applied after hot rolling. It could be concluded that both finish rolling temperature and the subsequent isothermal holding temperature were crucial for the achieved strength level due to the combined effect of grain refinement and precipitation hardening. At the same time, it was found that the isothermal holding led to poor impact toughness because of remarkable precipitation hardening. Therefore, it was suggested that the precipitation kinetics of titanium carbides in both austenite and ferrite should be investigated in future.
Abstract��Using the similar compositions of the Ti-microalloyed high-strength steels produced by the thin-slab casting process of compact strip production (CSP), four thermo-mechanical control processes(TMCP) after the simulated thick-slab casting, i.e. the two hot rolling routes and the two cooling processes, were designed, aiming at achieving the same mechanical properties as the thin strip products. The final microstructures after the four TMCP processes were examined by optical microscope(OM), scanning electron microscope(SEM) and transmission electron microscope (TEM). The tensile properties and Charpy impact energy were measured correspondingly. Strain-induced TiC precipitation was found in the two-stage rolling route with the finish rolling temperature at low levels, leading to grain refinement due to the pinning effect during austenite recrystallization. Precipitation hardening in ferrite was observed when a period of isothermal holding was applied after hot rolling. It could be concluded that both finish rolling temperature and the subsequent isothermal holding temperature were crucial for the achieved strength level due to the combined effect of grain refinement and precipitation hardening. At the same time, it was found that the isothermal holding led to poor impact toughness because of remarkable precipitation hardening. Therefore, it was suggested that the precipitation kinetics of titanium carbides in both austenite and ferrite should be investigated in future.
Xiang-dong HUO,Lie-jun LI,Zheng-wu PENG,Song-jun CHEN. Effects of TMCP Schedule on Precipitation, Microstructure and Properties of Ti-microalloyed High Strength Steel[J]. �й������ڿ���, 2016, 23(6): 593-601.
Xiang-dong HUO,Lie-jun LI,Zheng-wu PENG,Song-jun CHEN. Effects of TMCP Schedule on Precipitation, Microstructure and Properties of Ti-microalloyed High Strength Steel. Chinese Journal of Iron and Steel, 2016, 23(6): 593-601.
2016, Vol. 23 
