Effect of cellular recrystallization on tensile properties of a nickel-based single crystal superalloy containing Re and Ru
Zhen-xue Shi,Shi-zhong Liu,Xiao-dai Yue,Li-jie Hu,Wan-peng Yang,Xiao-guang Wang,Jia-rong Li
Science and Technology on Advanced High Temperature Structural Materials Laboratory, Beijing Institute of Aeronautical Materials, Beijing 100095, China
Effect of cellular recrystallization on tensile properties of a nickel-based single crystal superalloy containing Re and Ru
Zhen-xue Shi,Shi-zhong Liu,Xiao-dai Yue,Li-jie Hu,Wan-peng Yang,Xiao-guang Wang,Jia-rong Li
Science and Technology on Advanced High Temperature Structural Materials Laboratory, Beijing Institute of Aeronautical Materials, Beijing 100095, China
ժҪ A nickel-based single crystal superalloy containing Re and Ru was cast in a directional solidification furnace. The single crystal specimens after standard heat treatment were grit blasted with different pressures and then heat treated at 1100��C for 4 h under vacuum condition. The evolution of recrystallized microstructure and its effect on the tensile properties at 850 and 980��C were investigated. After heat treatment, the cellular microstructure was observed, and the thickness of the cellular recrystallization zone increases with the increase in grit blasting pressure. The appearance of the cellular structure undermines the tensile properties. Both the tensile strength and elongation decrease with increasing the thickness of the cellular structure. The recrystallized grain boundaries can act as the channels for the crack initiation and propagation during tensile test. The low bearing capacity of recrystallized layers and the local stress concentration resulting from the notch effect of cracking were the main reasons for the decrease of tensile properties.
Abstract��A nickel-based single crystal superalloy containing Re and Ru was cast in a directional solidification furnace. The single crystal specimens after standard heat treatment were grit blasted with different pressures and then heat treated at 1100��C for 4 h under vacuum condition. The evolution of recrystallized microstructure and its effect on the tensile properties at 850 and 980��C were investigated. After heat treatment, the cellular microstructure was observed, and the thickness of the cellular recrystallization zone increases with the increase in grit blasting pressure. The appearance of the cellular structure undermines the tensile properties. Both the tensile strength and elongation decrease with increasing the thickness of the cellular structure. The recrystallized grain boundaries can act as the channels for the crack initiation and propagation during tensile test. The low bearing capacity of recrystallized layers and the local stress concentration resulting from the notch effect of cracking were the main reasons for the decrease of tensile properties.
Zhen-xue Shi,Shi-zhong Liu,Xiao-dai Yue,Li-jie Hu,Wan-peng Yang,Xiao-guang Wang,Jia-rong Li. Effect of cellular recrystallization on tensile properties of a nickel-based single crystal superalloy containing Re and Ru[J]. �й������ڿ���, 2017, 24(10): 1059-1064.
Zhen-xue Shi,Shi-zhong Liu,Xiao-dai Yue,Li-jie Hu,Wan-peng Yang,Xiao-guang Wang,Jia-rong Li. Effect of cellular recrystallization on tensile properties of a nickel-based single crystal superalloy containing Re and Ru. Chinese Journal of Iron and Steel, 2017, 24(10): 1059-1064.
CARON P, KHAN T. Evolution of Ni-based superalloys for single crystal gas turbine blade applications [J]. Aerospace Science Technology, 1999, 3: 513�C523.
[2]
ARGENCE D, VERNAULT C, DESVALLEES Y, FOURNIER D. MC-NG: Generation single crystal superalloy for future aeronautical turbine blades and vanes [C]//Superalloys 2000. Warrendale: TMS, 2000: 829?837.
[3]
WALSTON S, CETEL A, MACKAY R, O��HARA K, DUHL D, DRESHFIELD R. Joint development of a fourth generation single crystal superalloy [C]//GREEN K A, POLLOK T M, HARADA H, HOWSON T W, REED R C, SCHIRRA J J, WALSTON S. Superalloys 2004. Pennsylvania: TMS, 2004: 15?24.
[4]
RETTBERG L H, POLLOCK T M. Localized recrystallization during creep in nickel-based superalloys GTD444 and Rene��N5 [J]. Acta Materialia, 2014, 73: 287�C297.
[5]
ZHANG B, LU X, LIU D L, TAO C H. Influence of recrystallization on high-temperature stress rupture property and fracture behavior of single crystal superalloy [J]. Materials Science and Engineering A, 2012, 551: 149�C153.
[6]
XIONG J C, LI J R, LIU S Z. Surface recrystallization in Nickel base single crystal superalloy DD6 [J]. Chinese Journal of Aeronautics, 2010, 23: 478�C485.
[7]
XIONG J C, LI J R, SUN F L, LIU S Z, HAN M. Microstructure of recrystallization and their effects on stress rupture property of single crystal superalloy DD6 [J]. Acta Metallurgica Sinica, 2014, 50(6): 737�C743.(in chinese)
[8]
ZAMBALDI C, ROTERS F, RAABE D, GLATZEL U. Modeling and experiments on the indentation deformation and recrystallization of a single-crystal nickel-base superalloy [J]. Materials Science and Engineering A, 2007, 454�C455: 433�C440.
[9]
COX D C, ROEBUCK B, RAE C M, REED R C. Recrystallisation of single crystal superalloy CMSX- 4 [J]. Materials Science and Technology, 2003, 19: 440�C445.
[10]
WEI W J, TANG H J, FENG Q. Effects of Surface Treatment on Cellular Recrystallization of a second generation single crystal superalloy [J]. Journal of Material Engineering, 2011, (8): 42�C47. (in chinese)
[11]
HE Y H, HOU X Q, TAO C H, HAN F K. Recrystallization and fatigue fracture of single crystal turbine blades [J]. Engineering Failure Analysis, 2011, 18: 944�C949.
[12]
MENG J, JIN T, SUN X F, HU Z Q. Effect of surface recrystallization on the creep rupture properties of a nickel-base single crystal superalloy [J]. Materials Science and Engineering A, 2010, 527: 6119�C6122.
[13]
MA X, SHI H J, GU J, YANG Z, CHEN G, LUESEBRINK O, HARDERS H. Influence of surface recrystallization on the low cycle fatigue behaviour of a single crystal superalloy [J]. Fatigue and Fracture of Engineering Material and Structure, 2015, 38: 340�C351.
[14]
MENG J, JIN T, SUN X F, HU Z Q. Surface recrystallization of a single crystal nickel-base superalloy [J]. International Journal of Minerals, Metallurgy and Materials, 2011, 18(2): 197�C202.
[15]
SHI Z X, LIU S Z, LI J R, HAN M. Microstructure evolution of boundaries with different angles in single crystal Ni-based superalloy during high temperature oxidation process [J]. Materials for Mechanical Engineering, 2013, 37(12): 75�C79. (in chinese)
[16]
ZHANG B, CHAO X G, LIU D L, LIU X L. Surface recrystallization of single crystal nickel-based superalloy [J]. Transaction Nonferrous Metals Society of China, 2013, 23: 1286?1292.
[17]
P. Wei, J.R. Li, Z.G. Zhong [J]. Mater. Eng. (10), 5(2001) (in Chinese)
[18]
Jo C Y, Cho H Y, Kim H M. Effect of recrystallisation on microstructural evolution and mechanical properties of single crystal nickel base superalloy CMSX-2 part 2-creep behavior of surface recrystallised single crystal [J]. Material Science and Technology, 2003, 19(12): 1671-1676.
[19]
Porter A, Ralph B. The recrystallization of nickel-base superalloys [J]. Journal of Materials Science, 1981, 16(3): 707-713.