1 School of Metallurgy, Northeastern University, Shenyang 110819, Liaoning, China 2 Northeastern Institute of Metal Materials Co., Ltd, Shenyang 110108, Liaoning, China
Modeling assessment of recovering iron from red mud by direct reduction: magnetic separation based on response surface methodology
1 School of Metallurgy, Northeastern University, Shenyang 110819, Liaoning, China 2 Northeastern Institute of Metal Materials Co., Ltd, Shenyang 110108, Liaoning, China
ժҪ Red mud, the waste generated during alumina production, contains iron and other valuable metals. To recover the iron efficiently from red mud, a three-factor five-level central composite design in response surface methodology was used to study the effects of process parameters, such as FC/O (the molar ratio of fixed carbon in coal to reducible oxygen of iron oxide in red mud), reduction temperature, reduction time, and their interaction on the iron recovery rate and total iron content in magnetic product obtained from the process of direct reduction�Cmagnetic separation. The relevant assessment model was established. The model could predict the changing rules of iron recovery rate and total iron content in the magnetic product affected by the process parameters. The results show that the iron recovery rate is significantly influenced by three factors and reduction temperature plays the most important role. The iron recovery rate and total iron content in magnetic product could be up to 98.37 and 82.52%, respectively, under the numerically optimal process parameters condition of reduction temperature of 1400 ��C, FC/O of 0.80 and reduction time of 100 min obtained by the assessment model. The predicted values are in good agreement with the experimental values.
Abstract��Red mud, the waste generated during alumina production, contains iron and other valuable metals. To recover the iron efficiently from red mud, a three-factor five-level central composite design in response surface methodology was used to study the effects of process parameters, such as FC/O (the molar ratio of fixed carbon in coal to reducible oxygen of iron oxide in red mud), reduction temperature, reduction time, and their interaction on the iron recovery rate and total iron content in magnetic product obtained from the process of direct reduction�Cmagnetic separation. The relevant assessment model was established. The model could predict the changing rules of iron recovery rate and total iron content in the magnetic product affected by the process parameters. The results show that the iron recovery rate is significantly influenced by three factors and reduction temperature plays the most important role. The iron recovery rate and total iron content in magnetic product could be up to 98.37 and 82.52%, respectively, under the numerically optimal process parameters condition of reduction temperature of 1400 ��C, FC/O of 0.80 and reduction time of 100 min obtained by the assessment model. The predicted values are in good agreement with the experimental values.
Ran Wang, Zheng-gen Liu Man-sheng Chu Hong-tao Wang Wei Zhao Li-hua Gao. Modeling assessment of recovering iron from red mud by direct reduction: magnetic separation based on response surface methodology[J].Journal of Iron and Steel Research International, 2018, 25(5): 497-505.
Ran Wang, Zheng-gen Liu Man-sheng Chu Hong-tao Wang Wei Zhao Li-hua Gao. Modeling assessment of recovering iron from red mud by direct reduction: magnetic separation based on response surface methodology. , 2018, 25(5): 497-505.
2018, Vol. 25 