1 The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan 430081, Hubei, China; 2 Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan University of Science and Technology, Wuhan 430081, Hubei, China; 3 Wuhan Branch of Baosteel Central Research Institute, Wuhan 430083, Hubei, China
Research progress on multiscale structural characteristics and characterization methods of iron ore sinter
1 The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan 430081, Hubei, China; 2 Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan University of Science and Technology, Wuhan 430081, Hubei, China; 3 Wuhan Branch of Baosteel Central Research Institute, Wuhan 430083, Hubei, China
摘要 At present, blast furnace ironmaking is still the main process for producing molten iron, and sinters are the main raw material for blast furnace ironmaking. A sinter with good metallurgical performance can not only ensure smooth operation of the blast furnace but also reduce the blast furnace fuel ratio and increase the molten iron production. Structure is the most important factor affecting the metallurgical properties of the sinter. Thus, the research progress of sinter pore and mineral phase structures was reviewed and the mechanism by which they influence sinter properties was expounded. Multiscale characterization methods for the sinter and their advantages and disadvantages were introduced, and the future research direction of sinter was discussed.
Abstract:At present, blast furnace ironmaking is still the main process for producing molten iron, and sinters are the main raw material for blast furnace ironmaking. A sinter with good metallurgical performance can not only ensure smooth operation of the blast furnace but also reduce the blast furnace fuel ratio and increase the molten iron production. Structure is the most important factor affecting the metallurgical properties of the sinter. Thus, the research progress of sinter pore and mineral phase structures was reviewed and the mechanism by which they influence sinter properties was expounded. Multiscale characterization methods for the sinter and their advantages and disadvantages were introduced, and the future research direction of sinter was discussed.
Wei Wang,Xu‑heng Chen,Run‑sheng Xu, et al. Research progress on multiscale structural characteristics and characterization methods of iron ore sinter[J]. Journal of Iron and Steel Research International, 2020, 27(4): 367-379.