Prediction of compressive strength based on visualization of pellet microstructure data
Ai-min Yang1,2, Yun-xi Zhuansun1
1 College of Science, North China University of Science and Technology, Tangshan 063210, Hebei, China; 2 College of Metallurgy and Energy, North China University of Science and Technology, Tangshan 063210, Hebei, China
Prediction of compressive strength based on visualization of pellet microstructure data
Ai-min Yang1,2, Yun-xi Zhuansun1
1 College of Science, North China University of Science and Technology, Tangshan 063210, Hebei, China; 2 College of Metallurgy and Energy, North China University of Science and Technology, Tangshan 063210, Hebei, China
摘要 In recent years, with the wide application of image data visual extraction technology in the field of industrial engineering, the development of industrial economy has reached a new situation. To explore the interaction between the pellet microstructure and compressive strength, firstly, the pellet microstructure needed for the experiment was obtained using a Leica DM4500P microscope. The area proportions of hematite, calcium ferrite, magnetite, calcium silicate and pore in pellet microstructure were extracted by visual extraction technology of image data. Moreover, the relationship between the area proportions of mineral components and compressive strength was established by backpropagation neural network (BPNN), generalized regression neural network (GRNN) and beetle antennae search-generalized regression neural network (BAS-GRNN) algorithms, which proves that the pellet microstructure can be used as the prediction standard of compressive strength. The errors of BPNN and BAS-GRNN are 5.13% and 3.37%, respectively, both of which are less than 5.5%. Therefore, through data visualization, we are able to discuss the connection between various components of pellet microstructure and compressive strength and provide new research ideas for improving the compressive strength and metallurgical performance of pellet.
Abstract：In recent years, with the wide application of image data visual extraction technology in the field of industrial engineering, the development of industrial economy has reached a new situation. To explore the interaction between the pellet microstructure and compressive strength, firstly, the pellet microstructure needed for the experiment was obtained using a Leica DM4500P microscope. The area proportions of hematite, calcium ferrite, magnetite, calcium silicate and pore in pellet microstructure were extracted by visual extraction technology of image data. Moreover, the relationship between the area proportions of mineral components and compressive strength was established by backpropagation neural network (BPNN), generalized regression neural network (GRNN) and beetle antennae search-generalized regression neural network (BAS-GRNN) algorithms, which proves that the pellet microstructure can be used as the prediction standard of compressive strength. The errors of BPNN and BAS-GRNN are 5.13% and 3.37%, respectively, both of which are less than 5.5%. Therefore, through data visualization, we are able to discuss the connection between various components of pellet microstructure and compressive strength and provide new research ideas for improving the compressive strength and metallurgical performance of pellet.
Ai-min Yang,Yun-xi Zhuansun. Prediction of compressive strength based on visualization of pellet microstructure data[J]. Journal of Iron and Steel Research International, 2021, 28(06): 651-660.
2021, Vol. 28 