Hot deformation behavior and microstructure features of FeCrAl–ODS alloy
1 Nuclear Power Institute of China, Chengdu 610213, Sichuan, China 2 School of Materials Science and Engineering, Central South University, Changsha 410083, Hunan, China
摘要 The hot deformation behavior of FeCrAl–ODS alloys at temperatures of 1050–1200 C and strain rates of 0.001–1 s-1 was investigated. The peak stress of FeCrAl–ODS alloy during hot deformation decreased with increasing temperature and decreasing strain rate. In addition, the stress–strain curves show a dynamic softening phenomenon according to the shape of the flow curves. Based on the Arrhenius-type model, a constitutive equation and processing map of FeCrAl–ODS alloy were established. Thereafter, we proposed optimum processing parameters of 1200 C and 0.001 s-1 based on the processing map. Compared with FeCrAl alloys, there was no significant phenomenon of grain coarsening during hot deformation in FeCrAl–ODS alloy. In the electron backscattered diffraction images, both recrystallized and recovered grains were observed in the matrix under different deformation conditions. The fraction of dynamically recrystallized grains in the matrix under the deformation of 1100 C/0.001 s-1 (42.5%) was significantly higher than that at 1200 C/ 0.001 s-1 (10.6%), which was consistent with the stress–strain curves.
Abstract:The hot deformation behavior of FeCrAl–ODS alloys at temperatures of 1050–1200 C and strain rates of 0.001–1 s-1 was investigated. The peak stress of FeCrAl–ODS alloy during hot deformation decreased with increasing temperature and decreasing strain rate. In addition, the stress–strain curves show a dynamic softening phenomenon according to the shape of the flow curves. Based on the Arrhenius-type model, a constitutive equation and processing map of FeCrAl–ODS alloy were established. Thereafter, we proposed optimum processing parameters of 1200 C and 0.001 s-1 based on the processing map. Compared with FeCrAl alloys, there was no significant phenomenon of grain coarsening during hot deformation in FeCrAl–ODS alloy. In the electron backscattered diffraction images, both recrystallized and recovered grains were observed in the matrix under different deformation conditions. The fraction of dynamically recrystallized grains in the matrix under the deformation of 1100 C/0.001 s-1 (42.5%) was significantly higher than that at 1200 C/ 0.001 s-1 (10.6%), which was consistent with the stress–strain curves.
Di-jun Long,Shao-yu Qiu,Wen-bo Liu, et al. Hot deformation behavior and microstructure features of FeCrAl–ODS alloy[J]. Journal of Iron and Steel Research International, 2022, 29(09): 1455-1463.