Effect of feeding parameters on ingot segregation and shrinkage pore in vacuum arc remelting
Dong-bin Jiang1, Fu-zhong Yang1, Jian Zhang2, Yang Zhou2, Li-feng Zhang3
1 School of Metallurgy and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China; 2 Chengdu Advanced Metal Materials Industrial Technology Institute, Chengdu 610303, Sichuan, China; 3 School of Mechanical and Materials Engineering, North China University of Technology, Beijing 100144, China
Effect of feeding parameters on ingot segregation and shrinkage pore in vacuum arc remelting
Dong-bin Jiang1, Fu-zhong Yang1, Jian Zhang2, Yang Zhou2, Li-feng Zhang3
1 School of Metallurgy and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China; 2 Chengdu Advanced Metal Materials Industrial Technology Institute, Chengdu 610303, Sichuan, China; 3 School of Mechanical and Materials Engineering, North China University of Technology, Beijing 100144, China
摘要 The feeding parameters in the final stage of vacuum arc remelting process obviously affect the solute segregation and shrinkage pore depth. Coupled with the electromagnetic field, fluid flow, and solute transport, a numerical model was built to investigate the effect of feeding parameters on the ingot solidification phenomena. The Nb segregation and shrinkage pore depth in the solidified ingot were measured. The results show that the liquid moves along the solidification front and the vertex flow is formed in the liquid pool, which promotes solute transport. In the solidified ingot, the Nb segregation in the lower part is negative, while that in the upper part is positive. With the differential electrode applied, the positive segregation is slightly reduced but the segregation distribution remains unchanged. As the feeding current decreases, the positive segregation zone moves toward the ingot top surface, due to the final solidification position moving upward. With the feeding time extended, the positive segregation moves to the top surface and the shrinkage pore depth is reduced. As the feeding time is set at 12 min, the shrinkage pore depth can be reduced to 21 mm.
Abstract：The feeding parameters in the final stage of vacuum arc remelting process obviously affect the solute segregation and shrinkage pore depth. Coupled with the electromagnetic field, fluid flow, and solute transport, a numerical model was built to investigate the effect of feeding parameters on the ingot solidification phenomena. The Nb segregation and shrinkage pore depth in the solidified ingot were measured. The results show that the liquid moves along the solidification front and the vertex flow is formed in the liquid pool, which promotes solute transport. In the solidified ingot, the Nb segregation in the lower part is negative, while that in the upper part is positive. With the differential electrode applied, the positive segregation is slightly reduced but the segregation distribution remains unchanged. As the feeding current decreases, the positive segregation zone moves toward the ingot top surface, due to the final solidification position moving upward. With the feeding time extended, the positive segregation moves to the top surface and the shrinkage pore depth is reduced. As the feeding time is set at 12 min, the shrinkage pore depth can be reduced to 21 mm.
Dong-bin Jiang,Fu-zhong Yang,Jian Zhang, et al. Effect of feeding parameters on ingot segregation and shrinkage pore in vacuum arc remelting[J]. Journal of Iron and Steel Research International, 2023, 30(6): 1268-1278.
2023, Vol. 30 