| Effect of Al2O3/SiO2 ratio on morphology of complex calcium ferrite |
| Dai-wei Yang1, Wei Wang2, Jing-xuan Li3, Xu-heng Chen2, Peng-fei Chen1 |
| 1 Jiangsu Yonggang Group Co., Ltd., Ironworks, Suzhou 215600, Jiangsu, China 2 Hubei Provincial Engineering Technology Research Center of Metallurgical Secondary Resources, Wuhan University of Science and Technology, Wuhan 430081, Hubei, China 3 Beijing Zhiye Interconnection Technology Co., Ltd., Beijing 100144, China |
|
|
|
|
Abstract Al2O3 and SiO2 greatly influence the formation of complex calcium ferrite, which is the main bonding phase in high basicity sinters. The effects of Al2O3/SiO2 ratios on the morphology of complex calcium ferrite were studied. The main mineral phases in the samples with different Al2O3/SiO2 ratios were CaFe2O4 with a solid solution of Si or Al atoms and the silico-ferrite of calcium and aluminum. The results showed that the morphology of the complex calcium ferrite changed from lumpy to plate-like and acicular with increases in the SiO2 content and the Al2O3/SiO2 ratio. When the content of SiO2 was 4 wt.%, the main calcium ferrite morphology was acicular, and the number of macropores in the samples increased with the Al2O3/SiO2 ratio increasing. The first-principles analysis of the calcium ferrite crystal structure showed that adding SiO2 and Al2O3 changed the growth mechanism of the CaFe2O4 crystal, promoting the formation of platy and acicular complex calcium ferrite. The size of calcium ferrite was significantly smaller due to the increase in CaO–Fe2O3– SiO2–Al2O3 viscosity with increasing the Al2O3/SiO2 ratio.
|
|
|
|
|
|
| Cite this article: |
|
Dai-wei Yang,Wei Wang,Jing-xuan Li, et al. Effect of Al2O3/SiO2 ratio on morphology of complex calcium ferrite[J]. Journal of Iron and Steel Research International, 2023, 30(10): 1921-1928.
|
|
|
|
| [1] |
Hai-hui Zhang, Hui-hui Xiong, Jing Qin, Jian-bo Zhang. Mechanism of ferrite nucleation induced by Y2O2S inclusion in low carbon steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2023, 30(6): 1291-1299. |
| [2] |
Feng Lu, Hong Zhong, Bo Liu, Jian Xu, Sheng-fu Zhang, Liang-ying Wen. Particle agglomeration behavior in fluidized bed during direct reduction of iron oxide by CO/H2 mixtures[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2023, 30(4): 626-634. |
| [3] |
Zi-tian Zhang, Jing-jing Wang, Wei Liu, Xiao-gang Lu. Simulation of BCC dissolution in Fe–Cr–Ni system by ICME[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2023, 30(4): 660-676. |
| [4] |
Chang Sun, Jing Li, Jie Zhang, Wei Yan, Shou-hui Li. Formation and evolution of primary carbides in high-carbon martensitic stainless steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2023, 30(10): 2000-2009. |
| [5] |
Yan-hui Hou, Ze-kun Xu, Guang-qiang Li. Effect of trace boron on corrosion resistance of rust layer of highstrength low-alloy steel in 3.5 wt.% NaCl solution[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2023, 30(10): 2080-2090. |
| [6] |
Fang Yuan, Zheng Zhao, Yan-ling Zhang, Tuo Wu. Influence of Cr2O3 content on viscosity and rheological behavior of Cr2O3-containing slags[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2022, 29(4): 601-611. |
|
|
|
|
2023, Vol. 30 