Causes analysis and control of peeling on low carbon Al-killed steel cold rolling substrate |
Yang Xiu-zhi |
(Valin Lianyuan Iron and Steel Co.,Ltd., Loudi 417009, Hunan, China) |
|
|
Abstract The cause of surface peeling defect on low carbon Al-killed steel cold rolling substrate in Lianyuan Steel is studied by means of optical metallographic microscope, SEM observation, energy spectrum analysis, slab examination after scarfing, and combined with process data statistics. The results show that the source of cold rolling substrate surface peeling is surface transversal crack on slab, which caused by secondary cooling condition in unstable case. By making control program of optimizing secondary cooling intensity and eliminating water leakage of segment, the quality problem of surface peeling on cold rolling substrate is effectively solved, the hot rolling reject percentage of this steel grade is observably reduced.
|
Received: 07 December 2017
Published: 16 March 2018
|
|
|
|
[1] |
赵新凯, 李刚利, 刘西峰, 鞠 伟. 冷轧低碳铝镇静钢表面起皮缺陷成因分析[J]. 物理测试, 2009, 27(5): 49-53
|
[2] |
祝桂合, 万友堂, 张继明, 杜恒科. 钢板表面裂纹及氧化物圆点形成条件模拟试验[J]. 山东冶金, 2012, 34(2): 30-33
|
[3] |
温维新. 中厚板边部裂纹缺陷的成因分析及对策[J]. 连铸, 2011, 6: 43-46
|
[1] |
WANG Yong, YANG Shu-feng, LI Jing-sheng, SU Rui-xian, YANG Jing-bo, ZHANG Fu-jun. Causes and control measures of corner transverse cracks in fine blanking steel continuous casting billet[J]. CONTINUOUS CASTING, 2022, 41(1): 49-55. |
[2] |
HUANG Yan, WANG Dong-xing, CHEN Yong-feng, YANG Wei-yong, ZHANG Qiang, WANG Wu-lei. Analysis and control of surface crack in high strength thread steel[J]. CONTINUOUS CASTING, 2020, 39(1): 40-45. |
[3] |
ZHAO Jing,WANG Zhen-ming,WANG Guo-lian,ZHEN Xin-gang,WANG Yu-long,HU Xian-tang. Research of casting technology on tail slab of 400 mm thick slab[J]. , 2019, 38(1): 1-4. |
[4] |
DU Chen- wei,,WANG Chun- lei,LI Bo,LI Bin,MA Bing- chuan,ZHANG Jia- quan. Effect of temperature field and cooling rate along casting direction on surface transverse cracks of microalloyed steel[J]. , 2018, 30(7): 523-528. |
[5] |
YANG Zhong-min,WANG Kai,SUN Xiu,DA Guang-jie. Grain boundary ferrite morphology and grain boundary crack in Nb/Ti microalloyed steel billets[J]. Iron and Steel, 2018, 53(11): 70-79. |
[6] |
ZHANG Jian-jun,,ZHANG Hui,XI Chang-suo,TAN Wen,WANG Chun-feng. Analysis and control of transverse corner cracking formation on middle carbon steel in thin slab casting[J]. Iron and Steel, 2017, 52(11): 32-36. |
|
|
|
|