Discussion about heat treatment process of X20Cr13 blade steel for gas turbine |
WANG Ji-hong, ZHANG Li-na, CHEN De-li, QI Yue, CAO Li-hong |
Technical Center, Fushun Special Steel Co., Ltd., Fushun 113001, China |
|
|
Abstract Different heat treatment processes were adopted to investigate the mechanical properties at room temperature, FATT and intergranular fracture rate of X20Cr13 blade steel. The results showed that the strength of the material increased with the increase of quenching temperature when the temper temperature was same. However, the impact toughness, FATT50 and intergranular fracture rate decreased. Good comprehensive mechanical properties could be obtained under heat treatment conditions of quenching at 970 ℃ and tempering at 670 ℃, which were suitable for the actual production.
|
Received: 13 June 2019
|
|
|
|
[1] |
WEI Tong-yu, ZOU De-ning, ZHANG Ying-bo, CHEN Wan-wan. Effect of aluminum on microstructure and properties of high alumina ferritic heat resistant steel[J]. Iron and Steel, 2020, 55(6): 80-83. |
[2] |
ZHAO Yun-peng, YU Chao, XIAO Hong, WU Zong-he, XU Peng-peng, XIE Hong-biao. Effect of pure iron interlayer on mechanical properties of hot rolled stainless steel clad plate[J]. Iron and Steel, 2020, 55(5): 73-79. |
[3] |
SHAO Cheng-wei, WANG Jun-tao, ZHAO Xiao-li, HUI Wei-jun. Microstructure and mechanical properties of intercritically annealed Al-contain medium Mn steel[J]. Iron and Steel, 2020, 55(5): 87-93. |
[4] |
XING Xian-qiang, CAO Wen-quan, WANG Cun-yu. Bond structure of 55SiCr steel used for coil springs of automotive suspension system[J]. Iron and Steel, 2020, 55(3): 68-73. |
[5] |
YANG Yu-dan,ZHAO Hong-shan,LIU Teng-shi,DONG Han. Microstructure and properties of new high-carbon martensitic stainless steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(2): 135-142. |
[6] |
YANG Geng-wei1,HU Zhuo-li1,YIN Qi-long1,MAO Xin-ping1,2,MIAO Li-sha1,LIU Yang2. Effect of phase transformation time on microstructure and mechanical properties of hotrolled TRIP steel produced by CSP process[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(2): 143-149. |
|
|
|
|