Cause analysis and improvement of brittle fracture #br# of HRB400 hot rolled ribbed steel bar |
XU Yan,GUO Zhan,WANG Debao,SONG Zufeng |
Maanshan Iron and Steel Co., Ltd.,Ma′anshan 243001, China |
|
|
Guide |
|
Abstract The brittle fracture of HRB400 hot rolled ribbed steel bar was inspected and analyzed by the means of chemical in-situ measurement, scanning electron microscopy (SEM) and metallographic structure examination. The results showed that the severe C and P segregation occurred in steel bar. Moreover, due to the rapid cooling rate after rolling in winter, many upper bainite structures with high strength and low plasticity were caused. There were some microcracks in local region of steel bar. In the case of bending, the stress concentration was formed at the cracks, which would expand rapidly. After repeated bending processing, the toughness of steel bar was reduced. These factors resulted in the brittle fracture of steel bar. On this basis, we put forward the corresponding improvement measures to the problem of brittle fracture of steel bar. The quality of HRB400 steel bar products had been improved, the brittle fracture phenomenon of steel bar did not occur in use.
|
Received: 18 June 2021
|
|
|
|
|
[1] |
ZHOU Da-qian, LU Heng-chang, LI Zhi-feng, WEI Xi-cheng, DONG Han. High temperature oxidation behavior and kinetics of HRB400 rebar[J]. Iron and Steel, 2022, 57(3): 108-114. |
[2] |
YAN Zhi, SHU Xing-zhong, LIU Ze-feng, LI Bin, JISHA Ri-fu, LUO Zhi-wen. Application of large size steel bar in engineering and its production technology transformation[J]. CONTINUOUS CASTING, 2022, 41(1): 78-81. |
[3] |
CHEN Lifei1, LUO Yunrong1, FU Lei1, LI Hui1, LI Xiulan1, ZHANG Yingqian2. Effects of salt spray corrosion on low cycle fatigue behavior and mechanical properties of HRB400E steel bar[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2021, 33(11): 1179-1188. |
[4] |
ZHAO Hai-sheng. Cause analysis of bending fracture of HRB400E hot-rolled ribbed steel bar[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(6): 50-. |
[5] |
KANG Jian, YU Yan-chong, MENG Xiao-liang, WANG She-bin. Research on cleanliness of HRB400E steel treated with rare earth[J]. CONTINUOUS CASTING, 2020, 39(3): 38-42. |
[6] |
LI Meng,SONG Xiao-jie. Reason analysis and improvement on the non-yield point of HRB400 wire rod[J]. Chinese Journal of Iron and Steel, 2017, 35(3): 7-9. |
|
|
|
|