Analysis and improvement of impact energy of high strength steel |
SHEN Yanjun |
Analysis and improvement of impact energy of high strength steel |
|
|
Abstract The average impact energy of 500 MPa grade highstrength steel is 18 J at -20 ℃. For the highstrength steel with unqualified impact energy, the microstructure of the steel plate was inspected by metallographic microscope. It was found that the size of ferrite was nonuniform, the microstructure of surface and core was different. Moreover, there were few pearlites in the core. The analysis showed that the reason to cause nonuniform size of ferrite was the partial recrystallization after the third stand of finish rolling, resulting in the nonuniform size of austenite, which was then inherited to the ferrite. Few pearlites in the core were due to the pearlite transformation from austenite under high coiling temperature and slow cooling speed. By increasing the finishing speed and reducing the coiling temperature, the problem of unqualified impact energy of 500 MPa highstrength steel was solved.
|
Received: 15 September 2021
|
|
|
|
[1] |
WANG Jin-feng, YUAN Yao, LI Cong. Microstructures and mechanical properties of laser tailor- welded dissimilar super-high strength steel sheets[J]. Iron and Steel, 2022, 57(9): 138-147. |
[2] |
DONG Jianxiong, GU Huazhi, HUANG Ao, XUE Zhengliang. Corrosion behavior of highalumina and lowsilicon CaOAl2O3 slags on corundum/calcium hexaaluminate based castables[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2022, 34(8): 825-833. |
[3] |
DING Kai1,2, DONG Wufeng1,2, WANG Li3,4, PAN Hua3,4, LEI Ming3,4, GAO Yulai1,2 . Progress and challenge of liquid metal embrittlement in galvanized advanced high strength steel
[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2022, 34(5): 399-410. |
[4] |
SU Xue, WANG Hou-xin, ZHU Min, ZHANG Qi, TIAN Jun-yu, XU Guang. In-situ observation for effect of niobium on pearlite transformation in high-carbon steels[J]. Iron and Steel, 2022, 57(4): 88-96. |
[5] |
ZHAO Yongtao, JIANG Yajun, LI Bobo, WANG Yufeng, REN Huiping. Effect of rare earth elements on microstructure evolution of low carbon microalloyed high strength steel during cooling[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2022, 34(2): 169-174. |
[6] |
LI Xue-tong, REN Ming-hua, LIU Ya-xing, SUN Ye-xuan, JIA Wen-qiang, TAN Chao-chao. Optimization of five-pass rolling schedule for high strength steel of 5+1 mill[J]. Iron and Steel, 2022, 57(2): 94-100. |
|
|
|
|