Defect analysis of 06Cr17Ni12Mo2 alloy ring forgings |
REN Qianguang,ZHANG Zheng,YANG Jiadian,YANG Lianghui,WANG Huadong,WU Yongan |
Gui Zhou Aviation Technology Development Co., Ltd., Guiyang 550081, China |
|
|
Abstract Excessive defects were found in the inner part of 06Cr17Ni12Mo2 alloy ring forgings during ultrasonic flaw detection. The defects would affect the properties of the forgings. They were easily exposed to the surface of the finished product in finishing process, which was very harmful. In order to analyze the reasons, the defects in 06Cr17Ni12Mo2 alloy ring forgings were detected by means of macroscopic examination, metallographic microscope and scanning electron microscope. The morphology and characteristics of the defects were confirmed. It was found that tested defects belonged to the typical AlSiO compound inclusions.
|
Received: 08 November 2021
|
|
|
|
[1] |
WANG Jing-zhong, YAO Hui-qin, ZHAO Ji-qing, YANG Xi-rong, YANG Gang, DING Kai-lun. Design and heat treatment of large-scale casting and forging materials for coal-fired power stations[J]. Iron and Steel, 2023, 58(2): 19-29. |
[2] |
ZHANG Li-feng, REN Ying. Concept of inclusion capacity of slag and its application[J]. Iron and Steel, 2023, 58(2): 47-60. |
[3] |
CAO Jian-qi, CHEN Chao, XUE Li-qiang, LI Zhou, ZHAO Jian, LIN Wan-ming. Analysis of inclusions in whole smelting process of non-oriented silicon steel DG47A[J]. Iron and Steel, 2023, 58(2): 61-71. |
[4] |
LI Yong-chao, YANG Yu-dan, LU Cai-ling, LI Cai-qing, WANG Wei. Evolution behavior of oxide inclusions in spring steel deoxidized by silicon during hot rolling[J]. Iron and Steel, 2023, 58(2): 83-89. |
[5] |
LI Xiang-long, SUN Qun, QU Tian-peng, WANG De-yong. Effect of electromagnetic stirring on the aggregation and removement of liquid inclusions in continuous casting mold[J]. CONTINUOUS CASTING, 2023, 42(1): 10-17. |
[6] |
NIU Shuai, DENG Wei, WANG De-jiong, HU Zhi-yong, WANG Kai-min, WANG Yu-hang, TANG Hai-yan. Effect of unsteady casting condition on cleanliness of tire cord steel[J]. CONTINUOUS CASTING, 2023, 42(1): 74-81. |
|
|
|
|