Analysis and improvement of drawing fracture of ER70S-6 welding wire steel |
CAO Lei 1,GUO Feng 2,JI Wenjie 1 |
1. Steel Rolling Mill, Jiangsu YongGang Group Co., Ltd., Zhangjiagang 215628, China;
2. R & D Department, Jiangsu YongGang Group Co., Ltd., Zhangjiagang 215628, China |
|
|
Abstract ER70S-6 welding wire rod broke during the fine drawing process. The microstructure of the wire rod was observed. The results showed that the drawing fracture of wire rod was caused by the abnormal microstructure, which could not deform synergistically with the pearlite + ferrite microstructure in the drawing process. Therefore, the cracks propagated and the fracture was caused. By controlling the segregation of components in the continuous casting process and optimizing the controlled rolling and controlled cooling process in the rolling process, the abnormal microstructure had been effectively decreased.
|
Received: 08 December 2021
|
|
|
|
[1] |
KONG Xiangwei,HOU Meiling,BAI Yun,LIN Zaiyong,ZHANG Xin. Discussion about slow strain rate test mechanical behavior of grade 10.9 high strength fastener steel[J]. PHYSICS EXAMINATION AND TESTING, 2022, 40(6): 7-. |
[2] |
YU Hui,CAO Jianhu,GAO Weiwei,REN Xintao. Determination of calcium fluoride content in fluorite spheres by instrumental analysis[J]. PHYSICS EXAMINATION AND TESTING, 2022, 40(6): 30-. |
[3] |
张小刚,俞东宝,汤慧,申俊华,葛腾. Study on activation properties of depleted uranium materials by high energy X ray[J]. PHYSICS EXAMINATION AND TESTING, 2022, 40(6): 57-. |
[4] |
SHAN Xianfei,LEI Na,SHEN Jie. Analysis of influencing factors in hole expansion test of automobile plates by acid pickling[J]. PHYSICS EXAMINATION AND TESTING, 2022, 40(5): 22-. |
[5] |
DING Kai1,2, DONG Wufeng1,2, WANG Li3,4, PAN Hua3,4, LEI Ming3,4, GAO Yulai1,2 . Progress and challenge of liquid metal embrittlement in galvanized advanced high strength steel
[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2022, 34(5): 399-410. |
[6] |
NI Ao1, LI Chengzhi1, ZHANG Wei2, YIN Teng3, LU Zhengdong3, XUE Zhengliang2 . Numerical simulation research on tuyere air supply characteristics of large blast furnace [J]. JOURNAL OF IRON AND STEEL RESEARCH , 2022, 34(5): 411-420. |
|
|
|
|