nalysis of unqualified causes of generator yoke Q345C heavy and wide plate |
ZHANG Xueling 1,LI Maolin 2 |
1.NCS Testing Technology Co.,Ltd., Beijing 100081,China;2. Nuclear and Radiation Safety Center,
Ministry of Ecology and Environment of the People′s Republic of China,Beijing 100082,China |
|
|
Abstract The phenomenon of unqualified ultrasonic flaw detection results of generator yoke Q345C heavy and wide plate was studied. The tensile testing machine, impact testing machine, metallographic microscope, scanning electron microscopy and energy dispersive spectrometer were employed for the comprehensive analysis including the tensile properties, impact performance, macroscopic morphology, inclusion, microstructure, macrographic morphology and spectral analysis. The causes for the unqualified ultrasonic flaw detection results of generator yoke Q345C heavy and wide plate were analyzed. The experimental results showed that it was due to a black defect zone at 23 mm from the lower surface of steel plate. The detected plane domain of defects was Ushaped. The defect width exceeded 70 mm. The main defects were oxide inclusions, holes and center porosity. In order to improve the qualification rate of ultrasonic inspection of generator yoke Q345C heavy and wide plate, all aspects of steelmaking should be strictly controlled to strengthen the steel refining, improve the purity of molten steel, reduce the oxygen content in molten steel, and control the content and morphology of inclusions in steel to improve the internal quality of billets.
|
Received: 17 November 2021
|
|
|
|
[1] |
LI Yong-chao, YANG Yu-dan, LU Cai-ling, LI Cai-qing, WANG Wei. Evolution behavior of oxide inclusions in spring steel deoxidized by silicon during hot rolling[J]. Iron and Steel, 2023, 58(2): 83-89. |
[2] |
NING Ying-yi. Practice and process research of Q235B on beam blank caster[J]. CONTINUOUS CASTING, 2023, 42(1): 118-123. |
[3] |
MENG Yao-qing, LI Jian-li, ZHU Hang-yu, WANG Kun-peng, WANG Wei. Crystallization of CaO-SiO2-Al2O3 based inclusions in solid steel killed by Si-Mn alloys[J]. Iron and Steel, 2022, 57(9): 65-74. |
[4] |
KANG Yong-lin, ZHU Guo-ming, JIANG Min, WANG Guo-lian, LIU Peng-tao, XU Hai-wei, XIE Cui-hong, WEI Yun-fei, SHEN Kai-zhao, LIU Yang. Slab continuous casting by big roll heavy reduction and extra thick plate rolled by low compression ratio[J]. Iron and Steel, 2022, 57(7): 95-105. |
[5] |
REN Qianguang,ZHANG Zheng,YANG Jiadian,YANG Lianghui,WANG Huadong,WU Yongan. Defect analysis of 06Cr17Ni12Mo2 alloy ring forgings[J]. PHYSICS EXAMINATION AND TESTING, 2022, 40(6): 36-. |
[6] |
MENG Yao-qing, LI Jian-li, ZHU Hang-yu, WANG Kun-peng. Effect of LF soft bubbling time on oxide inclusions in Si-killed spring steel[J]. Iron and Steel, 2022, 57(5): 48-54. |
|
|
|
|