Effect of coiling temperature on microstructure and properties of 800 MPa-level high hole expansion steel |
LIU Yang, LU Qianqian, GU Hairong, MA Cong, CHEN Zhong, TIAN Zhijun |
Technology Center, Maanshan Iron and Steel Co., Ltd., Ma′anshan 243000, China |
|
|
Abstract The microstructure, mechanical property and hole expansion property of 800 MPa-level hot-rolled acid-pickled hole expansion steel at different coiling temperatures were analyzed by optical microscope, scanning electron microscope, tensile tester and hole punching expansion tester. The results showed that the microstructure was mainly composed of ferrite + bainite when the coiling temperature was 450-600 ℃. With the increase of coiling temperature, the ferrite grains increased, while the volume fraction of bainite decreased gradually. The yield strength and tensile strength of the material were improved, the elongation had no significant change, and the hole expansion rate was reduced obviously. With overall consideration, when the coiling temperature was 450-500 ℃, the tensile strength was higher than 780 MPa, and the hole expansion rate was above 50%.
|
Received: 11 May 2023
|
|
|
|
[1] |
余冲,吴腾. 热轧贝氏体双相钢中组织对性能的影响[J]. 钢铁钒钛,2018(2):4.
|
[2] |
韩鹏,董毅,李维娟,等. 高强度热轧高扩孔钢的研制与开发[J]. 金属热处理,2016,41(6):4.
|
[3] |
石刚,胡家状,张军,等. 高强钢扩孔试验方法探讨[J]. 物理测试,2019,37(3):19.
|
[4] |
单显飞,雷娜,沈洁. 汽车酸洗板扩孔试验的影响因素分析[J]. 物理测试,2022,40(5):6.
|
[5] |
黄玉龙,张玉龙. 超高强度复相钢CP800的相变行为及热轧工艺研究[J]. 上海金属,2018,40(4):6.
|
[6] |
吴腾,吴润,熊维亮,等. 卷取温度对高强贝氏体双相钢组织性能的影响[J]. 材料热处理学报,2017,38(12):5.
|
[7] |
蔡明晖. 高延伸凸缘型铁素体/贝氏体钢的组织演变及力学行为[D]. 沈阳:东北大学,2009.
|
[8] |
李秋寒,郭子峰,张,等. 卷取温度对热轧高扩孔540HE钢组织和性能的影响[J]. 上海金属,2019(2):5.
|
[9] |
蔡明晖,丁桦,张建苏,等. 经济型铁素体/贝氏体高扩孔钢的组织与性能[J]. 钢铁,2008,43(8):5.
|
[10] |
左建强. 冷却工艺对热轧高扩孔钢组织与性能的影响[J]. 中国金属通报,2018(10):2.
|
[11] |
张正群,邵建平,汪健宏,等. 高强汽车大梁钢折弯开裂原因分析[J]. 物理测试,2022,40(1):7.
|
[12] |
赵燕青,刘宏强,苏振军,等. 轧后中冷温度对780 MPa级高扩孔钢组织与性能的影响[J]. 金属热处理,2017,42(9):4.
|
[1] |
LI Shengcun, MIAO Chengliang, TIAN Guichang. Microstructure uniformity control of low carbon steel in short process continuous casting and rolling[J]. CONTINUOUS CASTING, 2024, 43(1): 62-66. |
[2] |
SHAN Xianfei,LEI Na,SHEN Jie. Analysis of influencing factors in hole expansion test of automobile plates by acid pickling[J]. PHYSICS EXAMINATION AND TESTING, 2022, 40(5): 22-. |
[3] |
WANG Yanguo. Analysis and investigation on the reason for unqualified mechanical properties of Q345T steel sheet pile[J]. PHYSICS EXAMINATION AND TESTING, 2022, 40(5): 37-. |
[4] |
LI Cheng-gang, SHAN Wen-chao, LIU Yi-si, YANG Ming, WANG Hao, CAO Guang-ming. Corrosion resistance process based on control of oxide scale in whole process of hot rolling[J]. Iron and Steel, 2021, 56(9): 129-135. |
[5] |
QIU Mu-sheng, ZHU Hao, HAN Yun, HAN Long-shuai, TENG Hua-xiang. Effect of annealing process on microstructure and properties of 780 MPa cold rolled multiphase steel[J]. Iron and Steel, 2021, 56(7): 139-144. |
[6] |
LI Hai-jun, LI Tian-xiang, LI Rui-hao, WANG Zhao-dong, WANG Guo-dong. Effect of direct rolling process on microstructure and mechanical properties of hot-rolled steel plate[J]. Iron and Steel, 2021, 56(4): 64-69. |
|
|
|
|