热处理工艺对超级马氏体钢逆变奥氏体的影响

  • 姜雯1,赵昆渝1,业冬1,李俊1,苏杰2,雍岐龙2
作者信息 +

Effect of heat treatment technology on reversed austenite in super martensitic stainless steel

  • 姜雯1,赵昆渝1,业冬1,李俊1,苏杰2,雍岐龙2
Author information +
文章历史 +

摘要

试验采用光学显微镜、X射线衍射仪(XRD)、透射电镜(TEM)及能谱分析(EDS)等手段,研究不同铬含量的超级马氏体不锈钢在相同热处理工艺下逆变奥氏体含量、组织形貌及生长规律的异同。结果表明,13Cr和15Cr两试验钢经淬火+回火后的显微组织为回火马氏体和逆变奥氏体,两试验钢中逆变奥氏体含量及尺寸均随着回火温度升高先增加再减小,且在650~700 ℃时达到最大。两试验钢内的逆变奥氏体在回溶过程中会对基体组织产生细化作用。通过对比发现,15Cr钢中的逆变奥氏体含量更多,尺寸更大,回溶时对基体的细化作用更明显。

Abstract

Beijing 100081, China) The effect of adding different content of Cr to the super martensitic stainless steel (SMSS) on formation of reversed austenite subjected to quenching and tempering by using optical microscope(OM), X-ray diffraction (XRD), transmission electron microscope (TEM) and energy dispersive spectrometer(EDS) was studied. The experimental results indicate that the microstructures of two tested steels were tempered martensite and reversed austenite after tempering. The volume fraction and grain size of reversed austenite in two tested steels increased first and then decreased with the increase of tempering temperature, which reached the maximum at 650-700 ℃. When the reversed austenite re-dissolved and transformed to martensite, there was an effect of refinement on the matrix. Compared with 13Cr steels, the reversed austenite in 15Cr steels was more and the size was bigger. The effect of refinement on the matrix was more obvious.

关键词

超级马氏体不锈钢 / 逆变奥氏体,铬 /

图表

引用本文

导出引用
姜雯, 赵昆渝, 业冬, . 热处理工艺对超级马氏体钢逆变奥氏体的影响[J]. 钢铁, 2015, 50(2): 70-75 https://doi.org/10.13228/j.boyuan.issn0449-749x.20140233
JIANG Wen, DIAO Hun-Yu, YE Dong, et al. Effect of heat treatment technology on reversed austenite in super martensitic stainless steel[J]. Iron and Steel, 2015, 50(2): 70-75 https://doi.org/10.13228/j.boyuan.issn0449-749x.20140233

参考文献

[1] C.A.D. Rodrigues, P.L.D. Lorenzo, A. Sokolowski, C.A. Barbosa, J.M.D.A. Rollo. Development of a Supermartensitic Stainless Steel Microalloyed with Niobium[J]. J ASTM, 2006, (3): 1-5.
[2] De-ning ZOU, Ying HAN, Wei ZHANG, Xu-dong FANG. Influence of tempering process on mechanical properties of 00Cr13Ni4Mo supermartensitic stainless steel[J]. Journal of Iron and Steel Research, 2010, (17): 50-54.
[3] Linne CP, Blanchard F, Guntz GC, Orlans-Joliet BJ. Corrosion performances of modified 13Cr for OCTG in oil and gas environments[J]. Corrosion, 1997, (97): 9-20.
[4] P.D. Bilmes, M. Solari, C.L. Llorente. Characteristics and effects of austenite resulting from tempering of 13Cr-NiMo martensitic steel weld metals[J].Materials Characterization, 2001, (46): 285-296.
[5] Hubackova J, Cihal V, Mazanec K. Two-Stage Tempering of steel 13%Cr6%Ni[J]. Materialwissenschaft und Werkstofftechnik, 1984, (15): 411-415.
[6] D. J. Dyson, B. Holmes. Effect of alloying additions on the lattice parameter of austenite[J]. Iron and Steel Institute of Japan. 1970, (208): 469-474.

[7] F C Monkman, F B Cuff, N. J. Grant. Computation of Ms for stainless steels[J]. Metals Progress. 1957, (71): 94-96.
[8]G H Eichelman, F. C. Hull. The effect of composition on the temperature of spontaneous transforamtion of austenite or martensite in 18-8 type stainless steel[J]. Transactions of the ASM. 1953, (45): 77-104.

基金

超级马氏体不锈钢基础研究

Accesses

Citation

Detail

段落导航
相关文章

/