合理利用资源开发节钒型含镍铬HRB500E钢筋

戴晓天; 周和敏; 李卫; 齐渊洪; 王长城

doi:10.13228/j.boyuan.issn0449-749x.20150208

钢铁 ›› 2016, Vol. 51 ›› Issue (1) : 76-81. DOI: 10.13228/j.boyuan.issn0449-749x.20150208

钢铁材料

合理利用资源开发节钒型含镍铬HRB500E钢筋

戴晓天¹，周和敏¹，李卫²，齐渊洪¹，王长城³

作者信息 +

Development of HRB500E rebar containing Ni/Cr and vanadium saving by rational resource utilization

戴晓天¹，周和敏¹，李卫²，齐渊洪¹，王长城³

Author information +

文章历史 +

摘要

根据企业原料特点（红土镍矿作为高炉炼铁配矿），提出充分利用铁水/钢水中的镍铬元素，开发资源节约型高强抗震钢筋的思路。在20MnSi钢的基础上，根据HRB500E级钢筋的性能要求进行成分设计，研究了镍、铬、钒等合金元素质量分数对钢筋力学性能的影响。结果表明，钢中镍、铬元素质量分数均为0.25%时，钒质量分数可以降低至0.062%，即满足HRB500E级钢筋的力学性能要求；而钢中不含镍、铬元素时，钒质量分数须达到0.11%才能满足性能要求。含镍铬HRB500E钢筋的钒加入量仅相当于不含镍铬的钒钢的56.36%，节钒效果显著。这种高强钢筋生产方法不仅节约了钒资源，还实现了对难处理的低品质红土镍矿的有效利用。

Abstract

A new method of producing resource saving， high strength， anti-seismic steel rebar was proposed， which could make full use of Ni， Cr elements in hot metal/liquid steel， as lateritic nickel ore was used as one of BF raw material. On the basis of 20MnSi steel， chemical components were designed according to the requirements of HRB500E grade rebar of China national standard. The effects of alloy elements， such as Ni， Cr and V on the mechanical properties of rebar were studied. The results show that， the mechanical properties of rebar met the requirements of HRB500E grade steel when the contents of Ni， Cr contents were 0.25% and the content of V reduced to 0.062%. As for the rebar which did not contain Ni， Cr elements， V content should reach 0.11% to meet the performance requirements of HRB500E grade. V content of HRB500E rebar which contains Ni and Cr is only equivalent to 56.36% of rebar without Ni and Cr. Hence， the effect of vanadium saving is obvious. This method not only saves the resource of vanadium， but also realizes the effective utilization of low-quality lateritic ore.

关键词

红土镍矿 / 钒微合金化 / 含镍铬钢筋 / 高强钢筋 / 抗震钢筋

Key words

lateritic nickel ore / vanadium micro-alloying / Ni, Cr containing rebar / high-strength rebar / anti-seismic rebar

图表

引用本文

EndNote

Ris (Procite)

Bibtex

导出引用

戴晓天, 周和敏, 李卫, 等. 合理利用资源开发节钒型含镍铬HRB500E钢筋[J]. 钢铁, 2016, 51(1): 76-81 https://doi.org/10.13228/j.boyuan.issn0449-749x.20150208

DAI Xiao-Tian, ZHOU He-Min, LI Wei, et al. Development of HRB500E rebar containing Ni/Cr and vanadium saving by rational resource utilization[J]. Iron and Steel, 2016, 51(1): 76-81 https://doi.org/10.13228/j.boyuan.issn0449-749x.20150208

参考文献

[1] 刘朝建. 持续推动高强度钢筋应用促进我国经济可持续发展[J]. 中国钢铁业. 2011, 12: 20.
LIU Chao-jian. Promoting high strength steel rebar’s application to boost sustainable development of China's economy[J]. China Steel. 2011, 12: 20.
[2] 祝学智, 范银平. 460MPa及500MPa级热轧带肋钢筋的研制与开发[J]. 冶金标准化与质量. 2002, 40(4): 1.
ZHU Xue-zhi, FAN Yin-ping. Development of 460MPa or 500MPa hot-rolled ribbed bar[J]. Metallurgical Standardization & Quality. 2002, 40(4): 1.
[3] 徐志, 韩斌, 吉玉. 500MPa级建筑钢筋的半工业试制[J]. 武钢技术. 2010, 48(5): 38.
XU Zhi, HAN Bin, JI Yu. Semi-industrial trial production of 500MPa grade reinforced bar for construction. WISCO Technology. 2010, 48(5): 38.
[4] 吴建军. HRB500( E)盘螺工艺优化[J]. 河北冶金. 2014, 220(4): 52.
WU Jian-jun. Process optimization of HRB500(E) coiled reinforced bar[J]. Hebei Metallurgy. 2014, 220(4): 52.
[5] 翁玉娟, 乔国平, 韩春良, 胡铁军. HRB500E高强抗震钢筋工艺优化[J]. 河北冶金. 2014, 220(4): 45.
WENG Yu-juan, QIAO Guo-ping, HAN Chun-liang, HU Tie-jun. Process optimization of HRB500E high-strength anti-seismic reinforced bar. Hebei Metallurgy. 2014, 220(4): 45.
[6] 崔培耀, 俞敏, 徐军. HRB500钢筋的试制开发[J]. 中国冶金. 2003, 13(11): 30.
CUI Pei-yao, YU Min, XU Jun. Development of HRB500 rein-bar[J]. China Metallurgy. 2003, 13(11): 30.
[7] 李璟, 范银平, 田晓霞. HRB500高强带肋钢筋研发与实践[J]. 河南冶金. 2012, 20(5): 19.
LI Jing, FAN yin-ping, TIAN Xiao-xia. Researching and practicing of HRB500 high strength ribbed bars[J]. Henan Metallurgy. 2012, 20(5): 19.
[8] 王洪锋, 王耀山. 钒氮微合金技术在 HRB500E开发中的应用[J]. 甘肃冶金. 2014, 36(2): 32.
WANG Hong-feng, WANG Yao-shan. Application of VN microalloying technology in HRB500E development. Gansu Metallurgy. 2014, 36(2): 32.
[9] 张红旭, 王栋. 建邦HRB500E高强抗震钢筋生产实践[J]. 山西冶金. 2013, 36(1): 73.
ZHANG Hong-xu, WANG Dong. Production practicing of high strength anti-seismic steel rebar in Jianbang Group Co. Ltd.[J]. Shanxi Metallurgy. 2013, 36(1): 73.
[10] 李卓. 酒钢 HRB500E 带肋钢筋的研制开发[J]. 酒钢科技. 2012, 3: 170.
LI Zhuo. Development of HRB500 ribbed steel bar in JISCO. JISCO Technology. 2012, 3: 170.
[11] 覃娟, 覃拥清. 柳钢高强度钢筋的推广和应用. 柳钢科技. 2013, 2: 51.
TAN Juan, Tan Yong-qing. Promotion and application of Liusteel’s high-strength rebar[J]. Liusteel Technology. 2013, 2: 51.
[12] 冯跃平. HRB500热轧带肋钢筋的生产试制[C]// 2012年高强度钢筋开发与应用推广技术及市场交流会. 北京: 中国钢铁工业协会, 2012: 165.
FENG Yue-ping. Trial production of HRB500 hot rolling ribbed steel bar[C]//High strength steel rebar development and application conference, 2012. Beijing: China Iron and Steel Association, 2012: 165.
[13] 孟庆宇. 西钢HRB500钢筋的工艺开发与实践[J]. 黑龙江冶金. 2012, 32(1): 48.
MENG Qing-yu. Process development and practice for HRB500 ribbed steel bars in Xilin Steel[J]. Heilongjiang Metallurgy. 2012, 32(1): 48.
[14] 王绍荣. Φ50mm大规格HRB500E抗震钢筋的试制[J]. 轧钢. 2011, 28(2): 67.
WANG Shao-rong. Development of Φ50mm large-sized HRB500E Seismic Reinforcement[J]. Steel Rolling. 2011, 28(2): 67.
[15] GB1499.2-2008, 钢筋混凝土用钢第2部分：热轧带肋钢筋[S]. 北京：中国标准出版社, 2008.
GB1499.2-2008, Steel for reinforcement of concrete- part 2: hot rolled ribbed bars[S]. Beijing: China Standard Press, 2008.
[16] 杨才福. 高强度建筑钢筋的最新技术进展[J]. 钢铁. 2010, 45(11): 1.
YANG Cai-fu. Recent developments of high strength rebars for building[J]. Iron and Steel. 2010, 45(11): 1.
[17] 杨才福, 张永权, 柳书平. 钒、氮微合金化钢筋的强化机制[J]. 钢铁. 2001, 36(5): 55.
YANG Cai-fu, ZHANG Yong-quan, LIU Shu-ping. Strengthening mechanism in V-N micro-alloyed reinforcing bar steels. Iron and Steel. 2001, 36(5): 55.