无镍高氮不锈钢弯曲疲劳裂纹萌生与扩展行为

  • 张慧芳,肖振兴,周 宇,钱丽华,王 薇,吕知清
作者信息 +

Bending fatigue crack initiation and propagation behaviors of a nickel free high nitrogen stainless steel

  • 张慧芳,肖振兴,周 宇,钱丽华,王 薇,吕知清
Author information +
文章历史 +

摘要

采用四点弯曲疲劳试验研究了不同应力水平下无镍高氮不锈钢的疲劳行为,并对材料疲劳裂纹的微观形貌、萌生位置及扩展路径进行了分析。结果表明,试验钢疲劳为多裂纹起裂,随着应力水平的升高,裂纹总长度逐渐增加,当应力水平接近材料屈服极限时,裂纹长度趋于稳定;裂纹大多数在滑移带处萌生,裂纹在扩展过程中产生了扭曲、偏移和分叉现象;裂纹在晶内主要沿单滑移带或多滑移带交替扩展,穿过晶界或孪晶界时大多发生了偏转。

Abstract

Using four-point bending fatigue test studied the fatigue behavior of nickel free high nitrogen stainless steel in different stress levels, and the micro morphology, initiation position and propagation trace of fatigue crack were analyzed. The fracture of experimental steel was multiple cracks, and the total crack length increased gradually with the increase of stress level. The crack length tends to be stable when the stress level was close to the yield limit of the material. Most of the cracks initiated at the slip zone, and the crack were distorted, migrated and bifurcated in the process of crack propagation. The crack propagated mainly along single slip band or multiple slip bands in the grain and deflected when crack crossed the grain boundary or twin boundary.

关键词

四点弯曲疲劳 / 无镍奥氏体钢 / 裂纹萌生 / 裂纹扩展 / 有限元

Key words

four-point bending fatigue / nickel free austenite steel / crack initiation / crack propagation / finite element method

图表

引用本文

导出引用
张慧芳, 肖振兴, 周宇, . 无镍高氮不锈钢弯曲疲劳裂纹萌生与扩展行为[J]. 钢铁, 2017, 52(10): 89-93 https://doi.org/10.13228/j.boyuan.issn0449-749x.20170158
ZHANG Hui-Fang, XIAO Zhen-Xin, ZHOU Yu, et al. Bending fatigue crack initiation and propagation behaviors of a nickel free high nitrogen stainless steel[J]. Iron and Steel, 2017, 52(10): 89-93 https://doi.org/10.13228/j.boyuan.issn0449-749x.20170158

基金

河北省自然科学基金项目(钢铁联合基金)

10

Accesses

0

Citation

Detail

段落导航
相关文章

/