大断面轴承钢控温轧制工艺与实验研究

  • 李胜利1,2,王国栋2,刘相华2,李瑛3
作者信息 +

Technics and Experimental Research on Controlled Rolling for LargeCrossSection Bearing Steel Parts

  • 李胜利1,2,王国栋2,刘相华2,李瑛3
Author information +
文章历史 +

摘要

在分析轴承钢高温奥氏体再结晶规律的基础上,提出了抑制网状碳化物的控温轧制工艺,即大断面轴承钢采用900 ℃终轧,轧后以大于3 ℃/s的冷速冷却到700~550 ℃。利用有限元技术,模拟分析了工艺的可行性。现场实验结果表明,网状碳化物级别合格率大幅提升到77.3%,效果显著。

Abstract

Based on the recrystallization laws of deformed austenite of bearing steel, a controlled rolling technology to inhibit net carbide was proposed with finishing rolling temperature at 900 ℃, cooling rate after rolling higher than 3 ℃/s and reheating temperature in the range of 700~550 ℃.The feasibility of this controlled rolling technology was studied by FEM simulation. The result of field test shows that the largecrosssection parts produced with new technology have excellent performance and qualification rate in terms of net grade was increased to 77.3%.

关键词

轴承钢 / 碳化物 / 控温轧制 / 网状

Key words

bearing steel / carbide / controlled rolling / net type

图表

引用本文

导出引用
李胜利, 王国栋, 刘相华, . 大断面轴承钢控温轧制工艺与实验研究[J]. 钢铁, 2007, 42(3): 41-0
LI Shengli, WANG Guodong, LIU Xianghua, et al. Technics and Experimental Research on Controlled Rolling for LargeCrossSection Bearing Steel Parts[J]. Iron and Steel, 2007, 42(3): 41-0

9

Accesses

0

Citation

Detail

段落导航
相关文章

/